Low-e glass plate, protective sheet for low-e glass plate and use thereof

ABSTRACT

Provided is a Low-E glass plate protection method capable of preventing or inhibiting alteration and erosion of Low-E layers. The protection method includes a step of applying a protective sheet to a surface of a Low-E glass plate having a Low-E layer comprising a tin component. Here, the Low-E layer comprises a tin component. The protective sheet has a PSA layer. The PSA layer comprises a phosphorus compound having a P—OR group. Here, R is a hydrogen atom or an organic group.

TECHNICAL FIELD

The present invention relates to a method for protecting a Low-E glass plate, a method for preventing/inhibiting alteration and the like to Low-E glass plates, a method for producing a glass unit, a laminate and a protective sheet for a Low-E glass plate.

The present application claims priority to Japanese Patent Application No. 2019-120485 filed on Jun. 27, 2019, the entire content thereof is incorporated herein by reference.

BACKGROUND ART

In processing and transporting various articles, in known techniques to prevent damage (scratches, contamination, corrosion, etc.) of their surfaces, protective sheets are bonded to the surfaces for protection. The objects to be protected vary widely. For instance, protective sheets are used on glass plates bearing Low-E (Low-Emissivity) layers (or Low-E glass plates) as well. Low-E glass plates are preferably used as building materials such as window glass because of the effects of the Low-E layers to improve the efficiency to cool down and heat up indoor spaces. In producing a Low-E glass plate, usually, until a Low-E glass plate and another glass plate are assembled into a pair-glass (e.g. dual-pane glass) with the Low-E layer surface on the inside, a protective sheet is applied to the Low-E layer surface which will be otherwise left exposed. This protects the Low-E layer from damage, wearing, degradation, corrosion, etc. Conventional at documents related to methods for producing glass units include Patent Documents 1 and 2.

For the surface protection, as a removable bonding means, pressure-sensitive adhesive (or PSA; the same applies hereinafter) can be preferably used. In general, pressure-sensitive adhesive has characteristics of being in a soft solid (viscoelastic) state in a room temperature range and easily adhering to adherend under some pressure. A surface protective sheet using PSA typically has a PSA layer on one face of a substrate sheet formed of a material such as resin and is constituted so as to achieve a protection purpose when the PSA layer is applied to an adherend (an object to be protected). Conventional art documents disclosing PSA sheets usable as surface protective sheets include Patent Documents 3 to 6. Patent Document 3 discloses a surface protective sheet that protects the surface of a metal plate while it is being drawn. Patent Document 4 discloses a surface protective sheet for optical film such as polarizing plates. Patent Document 5 relates to a surface protective sheet for a self-cleaning hydrophilic coated plate. Patent Document 6 is directed to easy removal of a surface protective sheet for metal plates on which top coats are formed and to reduction of the degree of contamination caused by it.

CITATION LIST Patent Literature

-   [Patent Document 1] European Patent No. 2150669 -   [Patent Document 2] WO 2016/139318 -   [Patent Document 3] Japanese Patent Application Publication No.     2017-186517 -   [Patent Document 4] Japanese Patent No. 5719194 -   [Patent Document 5] Japanese Patent Application Publication No.     2012-131976 -   [Patent Document 6] Japanese Patent No. 3571460

SUMMARY OF INVENTION Solution to Problem

Protection of a Low-E glass plate with a protective sheet can block not only physical damage such as breakage and abrasion, but also the entrance of water, moisture, etc. Low-E glass plates are protected with protective sheets when exposed to external environments and subjected to processes such as processing and washing. Accordingly, protective sheets are required to have properties to prevent the degradation and corrosion in such environments. However, for Low-E glass plate transportation, storage and so on, protection with protective sheets sometimes needs to last for a long period; and even in such a case, protective sheets am expected to prevent the degradation and corrosion to satisfactory levels.

This invention has been made in view of these circumstances with an objective to provide a Low-E glass plate protection method capable of preventing or inhibiting alteration in Low-E layers. Other objectives of this invention include providing a Low-E glass plate alteration prevention/inhibition method, providing a Low-E glass plate, providing a glass unit production method, providing a laminate, and providing a protective sheet ter Low-E glass plates.

Solution to Problem

This Description provides a method for protecting a Low-E glass plate. The method includes a step of applying a protective sheet to a surface of a Low-E glass plate having a Low-E layer. Here, the Low-E layer comprises a tin component. The protective sheet has a PSA layer. The PSA layer comprises a phosphorous compound having a P—OR group. Here, R is a hydrogen atom or an organic group.

According to this method, alteration and erosion (or collectively “alteration” hereinafter) of a Low-E layer can be prevented or inhibited not only during the protection period with the protective sheet, but also after the protective sheet is removed. In particular, the tin component of the Low-E layer reacts with the phosphorous compound in the PSA layer to form a layer deposit, a sort of protective film, on the Low-E layer. In the presence of the layer deposit, the entry of an alteration-causing substance and the like from the outside can be blocked. By this, Low-E layer alteration can be prevented or inhibited. For instance, as a result of studies, the present inventors have acknowledged that chloride ions cause silver erosion in Low-E layers and have realized that ammonia in PSA may act on zine components of Low-E layers, causing alteration to the Low-E layers. It is thought that the product of reaction between the tin component of the Low-E layer and the phosphorous compound in the PSA layer is present in a layer form to block the entry of components capable of causing Low-E layer alteration as described above, thereby preventing or inhibiting Low-E layer alteration in Low-E glass plates. It is noted that the mechanism of protection by this method is not limited to the interpretation. Based on the above, according to the method, in addition to the protection by application of the protective sheet, the protective functionality after removal of the protective sheet can prevent or inhibit Low-E layer alteration.

It is noted that the “tin component” here refers to a tin-containing component, including tin metal, a compound comprising tin and other element (tin-based compound), a composite (tin-based composite) and a mixture (tin-based mixture). Tin-based compounds such as tin oxide are typical examples of the tin component.

In a typical embodiment of the art disclosed herein (encompassing the Low-E glass protection method, Low-E glass plate alteration prevention/inhibition method. Low-E glass plate, glass unit production method, laminate and Low-E glass plate protective sheet; the same applies hereinafter), after the protective sheet is applied to the Low-E glass plate, a film is newly formed on/in the Low-E layer. The film comprises P and Sn as its constituent elements. The film formed of the reaction product of the tin component of the Low-E layer and the phosphorous compound in the PSA layer should be interpreted without particular limitations; however, it is thought to block the entry of components capable of causing Low-E layer alteration. In an embodiment including this effect, Low-E layer alteration can be prevented or inhibited in a Low-E glass plate.

As used herein, the “film” formed on/in the Low-E layer encompasses a layer deposit that can be formed on the Low-E layer surface as well as a layer deposit that is internal to the Low-E layer and not exposed to the outside. The film may be a film extending along the Low-E layer or a film extending in the Low-E layer's thickness direction. In the art disclosed herein, the “film” formed on/in the Low-E layer includes a layer deposit in general that serves as a barrier capable of blocking an incoming component (alteration-causing substance, etc.); and it can be present in a state so-called passivation.

In some embodiments of the an disclosed herein, the film exists on an outer surface of the Low-E layer. According to this embodiment, the film on the Low-E layer's outer surface can block the entry of the component potentially causing Low-E layer alteration. In this embodiment, in the Low-E layer before the film formation, the tin component (typically a tin-containing layer; i.e. a layer including a tin component) typically exists on the outermost surface of the Low-E layer. In other embodiments, the film exists internal to the Low-E layer. According to this embodiment, the film internal to the Low-E layer can block the entry of the component potentially causing Low-E layer alteration. Such a film may exist, for instance, in scratches and cracks formed in the Low-E layer or near them. In this embodiment, in the Low-E layer before the film formation the tin component (typically a tin-containing layer) may typically exist internal to the Low-E layer.

In some preferable embodiments of the an disclosed herein, the film is formed within 24 hours after the protective sheet is applied to the surface of the Low-E glass plate. The film can be formed in short time after the application of the protective sheet in a prescribed environment including rom temperature (about 10° C. to 30° C.), so that the protecting effect on the Low-E layer can express at an early stage.

In some preferable embodiments of the art disclosed herein, the film has a thickness of 1 nm or greater and 20 nm or less. The film having such a thickness can preferably exhibit the Low-E layer protecting effect.

In some preferable embodiments of the art disclosed herein, the phosphorous compound is selected between a phosphate and a phosphite. The use of the phosphate or phosphite as the phosphorous compound, the effect of the art disclosed herein can be preferably obtained.

In some preferable embodiments of the art disclosed herein, the Low-E layer includes a tin-containing layer. In an embodiment where the Low-E layer includes a tin-containing layer, the film can be formed on an entire face of the Low-E layer. In a typical embodiment, the tin-containing layer is a tin oxide-containing layer.

The method according to some embodiments further includes a step of removing the protective sheet from the Low-E glass plate. Between the application and removal of the protective sheet to and from the Low-E glass plate, the method includes a step of subjecting the Low-E glass plate having the protective sheet applied thereon to at least one process selected from the group consisting of transportation, storage, processing, washing and handling. In an embodiment of such use of the Low-E glass plate, by using the Low-E glass plate protective sheet, protection of the Low-E glass plate is realized.

In some embodiments of the art disclosed herein, the Low-E glass plate has a width of 1 m or greater. The application of the protective sheet to the Low-E glass plate includes a step of entirely covering one face of the Low-E glass plate with at least one of the protective sheet. The use of such a broad protective sheet can protect a Low-E glass plate having a large surface area with one sheet or a few sheets.

In some embodiments of the art disclosed herein, the protective sheet is adhered to the Low-E glass plate with a 180° peel strength of 5 N/20 mm or less. By this, when the protection period ends, the protective sheet can be removed from the Low-E glass plate by relatively low peel force.

This Description provides a method for preventing or inhibiting alteration to a Low-E glass plate (or sometimes abbreviated to a “alteration prevention/inhibition method). The method comprises a step of providing a phosphorous compound having a P—OR group to a Low-E layer in a Low-E glass plate, the Low-E layer including a tin component. Here, R in the P—OR group is a hydrogen atom or an organic group. The method can prevent or inhibit Low-E layer alteration.

In a typical embodiment, after the phosphorous compound is provided to the Low-E layer, a film is newly formed on/in the Low-E layer. This film comprises P and Sn as its constituent elements. The film formed of the reaction product of the tin component and the phosphorous compound in the Low-E layer should be interpreted without particular limitations; however, it is thought to block the entry of components capable of causing Low-E layer alteration.

In some preferable embodiments, with a protective sheet having a PSA layer that comprises the phosphorous compound, the phosphorous compound is provided by applying the PSA layer to the Low-E layer. By this, the film formed of the reaction product of the Low-E, layer's tin component and phosphorous compound can be preferably formed, thereby preventing or inhibiting Low-E layer alteration.

This Description provides a Low-E glass plate having a Low-E layer. In the Low-E glass plate, the Low-E layer includes a film comprising P and Sn as its constituent elements. In the presence of the fin comprising P and Sn as its constituent elements, the entry of an alteration-causing substance and the like from the outside can be blocked; and therefore, the resulting Low-E glass plate can be of high quality with minimal defects (alteration, etc.).

This Description also provides a glass unit production method. The production method includes a step (A) of obtaining a Low-E glass plate having a Low-E layer; a step (B) of applying a protective sheet to a surface of the Low-E layer of the Low-E glass plate; an optional step (C) of subjecting the Low-E glass plate having the protective sheet applied thereon to at least one process selected from the group consisting of transportation, storage, processing, washing and handling; a step (D) of removing the protective sheet from the Low-E glass plate; and a step (E) of fabricating a glass unit using the Low-E glass plate. Here, the Low-E layer comprises a tin component. The protective sheet has a PSA layer. The PSA layer comprises a phosphorous compound having a P—OR group. Here, R is a hydrogen atom or an organic group. According to this production method, alteration of the Low-E layer can be prevented or inhibited; and therefore, the resulting glass unit can be of high quality with minimal defects (alteration, etc.).

This Description also provides a laminate. The laminate has a Low-E glass plate and a protective sheet protecting a surface of the Low-E glass plate. The Low-E glass plate has a Low-E layer comprising a tin component. The protective sheet has a PSA layer. The PSA layer comprises a phosphorous compound having a P—OR group. Here, R is a hydrogen atom or an organic group. According to the laminate in such an embodiment, the Low-E layer of the Low-E glass plate constituting the laminate is protected with the protective sheet having the aforementioned constitution and the entry of alteration-causing substance from the outside can be blocked with the layer deposit formed of the product of reaction between the phosphorous compound in the PSA layer and the tin component of the Low-E layer; and therefore, Low-E layer alteration can be prevented or inhibited.

This Description also provides a protective sheet used on a Low-E glass plate having a Low-E layer that comprises a tin component. The protective sheet has a PSA layer. The PSA layer comprises a phosphorous compound having a P—OR group. Here, R is a hydrogen atom or an organic group. With a Low-E glass plate protective sheet having the constitution, alteration of Low-layers can be prevented or inhibited.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 shows a schematic diagram to illustrate an embodiment of the glass unit production method.

FIG. 2 shows a cross-sectional diagram schematically illustrating an embodiment of the protective sheet.

FIG. 3 shows a TM image of a cross section of a Low-E layer in a verification test.

DESCRIPTION OF EMBODIMENTS

Preferred embodiments of the present invention are described below. Matters necessary to practice this invention other than those specifically referred to in this description can be understood by a person skilled in the art based on the disclosure about implementing the invention in this description and common technical knowledge at the time of application. The present invention can be practiced based on the contents disclosed in this description and common technical knowledge in the subject field.

As used herein, the term “PSA” refers to, as described earlier, a material that exists as a soft solid (a viscoelastic material) in a room temperature range and has a property to adhere easily to an adherend with some pressure applied. As defined in C. A. Dahlquist, “Adhesion: Fundamental and Practice” (McLaren & Sons (1966) P. 143), the PSA referred to herein is a material that has a property satisfying complex tensile modulus E* (1 Hz)<10⁷ dyne/cm² (typically, a material that exhibits the described characteristics at 25° C.).

The concept of protective sheet herein may encompass so-called PSA sheet. PSA tape. PSA labels, PSA film, etc. The protective sheet disclosed herein can be in a roll or in a flat sheet. Alternatively, the protective sheet may be processed into various shapes.

<Glass Unit Production Method>

The glass unit production method disclosed herein comprises a step (A) of obtaining a Low-E glass plate comprising a glass substrate and a Low-E layer placed on the glass substrate; a step (B) of applying a protective sheet to the Low-E layer surface of the Low-E glass plate; an optional step (C) of subjecting the Low-E glass plate with the protective sheet adhered thereon to at least one process selected from the group consisting of transportation, storage, processing, washing and handling; a step (D) of removing the protective sheet from the Low-E glass plate; and a step (E) of assembling a glass unit using the Low-E glass plate. In this method, the protective sheet (or surface-protective sheet) disclosed herein is used. Further description is provided below while referring to FIG. 1.

First, in the step (A), as shown in FIG. 1, a Low-E glass plate 100 having a Low-E layer 120 is obtained (S10). In particular, Low-E glass plate 100 can have a glass substrate 110 and a Low-E layer 120 placed on the glass substrate 110. Low-E glass plate 100 is obtained by forming Low-E layer 120 on one face of glass substrate 110. The Low-E layer comprises a metal layer, an oxide layer such as a metal oxide layer, and a nitride layer such as silicon nitride; usually has a multi-layer structure; and can be formed by a known or conventionally-used method such as sputtering. The size of the glass substrate is not particularly limited with one side (width) being, for instance, about 1 m or greater, or about 2 m or greater. Lately, pieces having surface areas larger than 2.6 m at one side, or even as large as about 3 m or greater (e.g. about 3.3 m or greater) at one side are used.

The materials forming the respective layers in the Low-E layer include TiO₂, ZrO₂, Si_(X)N_(Y), ZnO_(X), Ag, NiCrO_(X), SnO₂ and ZTO (oxide of zinc and tin). As an infrared-reflective layer, a Ag layer is preferably used. The Ag layer can be formed of Ag alone or an alloy of Ag and other metal (Pd, etc.). Low-E layer 120 in this embodiment includes a tin oxide layer. It may include a zinc-containing layer such as a zinc oxide layer. While no particular limitations are imposed, in the Low-E layer according to some embodiments, the Ag layer can be present between any two of oxide layers such as TiO₂ layers, ZrO₂ layers, ZnO_(X) layers, NiCrO_(X) layers, SnO₂ layers and ZTO layers or nitride layers such as Si_(X)N_(Y) layers. The material of the Low-E layer's outermost surface (to which the protective sheet is applied) is often an oxide such as TiO₂, ZrO₂, ZnO_(X), NiCrO_(X), SnO₂ and ZTO or a nitride such as Si_(X)N_(Y); it typically is not a metal such as Ag. Depending on the purpose and required properties, the Low-E layer may have a multi-layer structure with 5 or more layers, for instance, 10 or more layers, or even 15 or more layers. The thickness of each layer is not particularly limited. It is usually 1000 Å or less, or suitably about 10 Å to 700 Å, for instance, about 30 Å to 300 Å. The thickness (overall thickness) of the Low-E layer can be about 10 nm to 1000 nm (e.g. about 50 nm to 500 nm). The Low-E glass plate can be a generally available product or modified product thereof including commercial products, or can be prepared by a known or conventional method.

In the step (B), as shown in FIG. 1, a protective sheet 200 is applied to the surface of Low-E layer 120 formed on glass substrate 110 (S20). Protective sheet 200 is typically applied to the surface in a removable manner. Here, “(to be) applied in a removable manner” means adhesion whose eventual release is intended or expected; in many cases, it refers to adhesion such that the adherend can maintain its pre-adhesion surface condition basically intact after the protective sheet (PSA sheet) is removed. In particular, protective sheet 200 is applied to Low-E glass plate 100 by adhering the PSA layer surface of protective sheet 200 to the surface of Low-E layer 120 of Low-E glass plate 100. By this, the surface of Low-E glass plate 100 is protected with protective sheet 200. From the standpoint of the protection, the size of protective sheet 200 is preferably about the same as the surface of Low-E layer 120. Two or more protective sheets may be partially layered to cover the surface to be protected. By covering the surface of Low-E layer 120 with protective sheet 200, the Low-E layer 120 can be prevented or inhibited from alteration.

After the step (B), as the step (C), with respect to the Low-E glass plate 100 having the protective sheet 200 applied thereon, at least one process may be optionally carried out, selected from the group consisting of transportation, storage, processing, washing and handling (S30). The processing may be the sort of cutting and edge seaming of the Low-E glass plate 100 having the protective sheet 200 applied thereon. The cutting means and the cut size are suitably selected in accordance with the purpose and are not particularly limited. The protective sheet 200 may be left on the surface of Low-E layer 120 even after the Low-E glass plate 100 is cut. The cut Low-E glass plate 100 is typically washed with water, etc. In the washing step, in addition to the water, a detergent (including surfactant) may be optionally used. During the transportation, storage, processing such as cutting, washing such as a water wash and various kinds of handling, as shown in FIG. 1, by the presence of protective sheet 200 thereon, the Low-E layer 120 is protected from damage, wearing and alteration.

Subsequently, in the step (D), protective sheet 200 is removed from Low-E glass plate 100 (S40). The protective sheet 200 is removed from Low-E glass plate 100 (adherend) after achieving the protection purpose. Low-E glass plate 100 from which protective sheet 200 is removed is usually heated and annealed in an oven. Subsequently, as shown in FIG. 1, using the Low-E glass plate 100, a glass unit 300 is fabricated (S50). Glass unit 300 is typically a heat-blocking or thermally-insulating glass unit, which can be fabricated by obtaining a pair of glass plates of which at least one is a Low-E glass plate and assembling a pair-glass (e.g. dual-pane glass) with the surface of Low-E layer 120 of Low-E glass plate 100 on the inside. Numbers 320 and 340 in FIG. 1 represent another glass plate forming the glass unit 300 and a spacer, respectively. Spacer 340 is placed between Low-E glass plate 100 and another glass plate 320 to create an open space between glass plates 100 and 320. In the method disclosed herein, in addition to the protective sheet, known or conventionally-used powder or coating liquid may be used together.

The embodiment has been illustrated with an example of a Low-E glass plate having a tin oxide-containing Low-E layer; however, the Low-E glass plate is not limited to those having tin oxide-containing Low-E layers. In the art disclosed herein, the effect to prevent/inhibit Low-E layer alteration includes the effect based on the film formed of the product of reaction between the tin component of the Low-E layer and the phosphorous compound in the PSA layer. Thus, the Low-E layer used in this at is not particularly limited as long as it comprises a tin component.

The Low-E layer of the Low-E glass plate disclosed herein may typically has one, two or more tin-containing layers. One tin-containing layer has a thickness of, for instance, about 100 nm or less, or suitably about 70 nm or less (e.g. about 50 nm or less, or even about 30 nm or less) and, for instance, about 1 nm or greater, or suitably about 3 nm or grater (e.g. about 8 nm or greater). Typical examples of the tin-containing layer include a tin oxide-containing layer. The tin oxide-containing layer may be formed of tin oxide or an oxide of tin and other element (e.g. zine).

The tin oxide-containing layer may be present on the outer surface (outermost surface) or may be present inside the Low-E layer. In an embodiment where the tin-containing layer is present inside the Low-E layer, the distance (thickness) from the Low-E layer's outer surface to the tin-containing layer is not particularly limited. It is, for instance, about 300 nm or less, or suitably about 200 nm or less (e.g. about 100 nm or less. In such an embodiment, the effect of the art disclosed herein can be preferably obtained. The minimum distance (thickness) from the Low-E layer's outer surface to the tin-containing layer is not particularly limited. It can be, for instance, about 1 nm or greater, or even about 10 nm or greater.

<Protection Method>

The protection method disclosed herein uses the protective sheet (or surface protective sheet) disclosed herein. It is typically a method for partially or entirely protecting the surface of a Low-E glass plate. The protection method disclosed herein is characterized by comprising a step of applying the protective sheet to the surface of the Low-E glass plate (an application step). The method prevents or inhibits Low-E layer alteration. In particular, the protective sheet has a PSA layer and the PSA layer comprises a phosphorous compound having a P—OR group. When such a PSA layer is applied to a Low-E layer surface of a Low-E glass plate, the phosphorous compound in the PSA layer transfers to the Low-E layer surface and reacts with the tin component of the Low-E layer to form a film (which may be referred to as a “passivation film” for the convenience, hereinafter) as shown in FIG. 3 on the Low-E layer. The presence of the passivation film is thought to block the entry of an alteration-causing substance and the like from the outside. Based on the results of analysis in Examples described later, because the product of reaction between the P—OR-group-containing phosphorous compound and the tin component includes P and Sn as its constituent element, it is presumed to be formation of tin phosphate upon reaction of P—O⁻ and Sn; however, the art disclosed herein is not limited to this thought.

The film newly formed upon application of the protective sheet comprises P and Sn as its constituent elements as described above. The film may further comprise O as a constituent element thereof. The film may further comprise or may be free of C as its constituent element. The C-free film is formed of an inorganic substance. The film is formed within 24 hours after the protective sheet is applied to the surface of the Low-E glass plate. Thus, in this method, the time period for which the protective sheet is adhered on the Low-E glass plate can be about one day or more, for instance, three days or more, or even about one week or more (e.g. about two weeks or more). No particular limitations are imposed on the temperature during application of the protective sheet. It is preferably room temperature (about 10° C. to 30° C.) or higher (e.g. above 30° C. up to about 50° C.). No particular limitations are imposed on the humidity during application of the protective sheet. It can be, for instance, 50% RH (relative humidity). From the standpoint of the ease of film formation, it can also be 75% RH or higher (e.g. 90% RH or higher).

The film can be formed in an area where the tin component of the Low-E layer exists while the phosphorous compound that may be transferred from the PSA layer can make contact with or permeate through the area; and therefore, the film can be formed not only on the outer surface of the Low-E layer, but can also be formed internal to the Low-E layer. For instance, the film can be formed when the phosphorous compound enters the Low-E layer's interior via scratches and cracks formed in the Low-E layer and makes contact with the tin-containing layer placed internal to the Low-E layer. Thus, the film can exist on the outer surface of the Low-E layer or internal to the Low-E layer. The film may be arranged adjacent to the tin-containing layer. The film can extend along the Low-E layer or in the thickness direction of the Low-E layer. In some embodiments, the film can be formed entirely over the outer surface of the Low-E layer. In this embodiment, the outermost layer (initial outermost layer) of the Low-E layer can be a tin-containing layer such as a tin oxide layer. In the Low-E layer, the film can be directly layered atop the tin-containing layer.

The film thickness is not limited to a specific range. From the standpoint of preferably obtaining the Low-E layer protecting effect, it is suitably about 1 nm or greater, preferably 2 nm or greater, or more preferably 3 nm or greater, for instance, 5 nm or greater. The maximum film thickness is, for instance, about 20 nm or less, or suitably about 15 nm or less (e.g. about 10 nm or less). The film thickness can be determined based on TEM observation of a cross section in the Low-E layer.

The protection method disclosed herein may further comprise a step of removing the protective sheet from the Low-E glass plate (a removal step). Between the application step and the removal step, for the article having the protective sheet applied thereon, the method may optionally include at least one process selected from the group consisting of transporting, storing, processing, washing and handling.

A favorable example of the protection method disclosed herein is as described earlier regarding the glass unit production method; the application step and the removal step of this protection method correspond to the steps (B) and (D) in the production method, respectively. Other matters in the protection method are not particularly limited. They can be understood by an ordinarily-skilled person in consideration of the description of the glass unit production method. Thus, details are omitted here. The particulars regarding the protection method can also be applied to the glass unit production method.

<Low-E Glass Plate Alteration Prevention/Inhibition Method>

As understood from the above, the Low-E glass plate protection method disclosed herein includes forming a film on the Low-E layer by using the reaction between the tin component of the Low-E layer and a specific phosphorous compound in the PSA of the protective sheet. Thus, the art disclosed herein provides a Low-E glass plate alteration prevention/inhibition method using the film formation. The method is characterized by including a step of providing a P—OR-group-containing phosphorous compound to a Low-E layer of a Low-E glass plate, the Low-E layer including a tin component. According to the method, the tin component in the Low-E layer reacts with the phosphorous compound provided thereto to form a film of the reaction product on the Low-E layer. In the presence of the film, the entry of an alteration-causing substance and the like from the outside is blocked whereby alteration in the Low-E layer can be prevented or inhibited.

No particular limitations are imposed on the method for providing the P—OR-group-containing phosphorous compound to the Low-E layer of the Low-E glass plate. For instance, a liquid formula (e.g. possibly an aqueous solution) comprising the phosphorous compound is provided to the Low-E layer surface by means such as spraying, coating and dipping. In a preferable embodiment using a protective sheet having a PSA layer comprising the phosphorous compound, the phosphorous compound is provided by adhering the PSA layer surface to the Low-E layer. By this, the phosphorous compound in the PSA may transfer to the Low-E layer surface and react with the tin component of the Low-E layer to form a film. According to this method, the film can be formed in about one day after the phosphorous compound is provided to the Low-E layer of the Low-E glass plate. From the standpoint of forming a sufficiently thick film, the film formation period (film growth period) can be, for instance, about three days or more, or even about one week or more (e.g. about two weeks or more). The temperature for this is not particularly limited and is preferably room temperature (about 10° C. to 30° C.) or higher (e.g. above 30° C. up to about 50° C.). The humidity is not particularly limited and can be, for instance, 50% RH or higher. From the standpoint of film formation, it is preferably 75% RH or higher (e.g. 90% RH or higher). The details of the method regarding where the film is formed, constituent elements of the film, film thickness and so on are as described earlier, and thus are not repeated.

<Low-E Glass Plate>

As described above, according to the art disclosed herein, by providing a P—OR-group-containing phosphorous compound, an unconventional novel film is formed on/in a Low-E layer of a Low-E glass plate having the Low-E layer. This film can help prevent alteration of the Low-E layer. Thus, the at disclosed herein provides a Low-E glass plate having a novel Low-E layer. In the Low-E glass plate, the Low-E layer comprises P and Sn as its constituent elements. In the presence of the film comprising P and Sn as its constituent elements, the entry of an alteration-causing substance and the like from the outside can be blocked; and therefore, the resulting Low-E glass plate can be of excellent durability with minimal defects (alteration, etc.) and also of high quality. The details of the glass plate having the Low-E layer and of the film (conditions and locations for formation, constituent elements of the film, film thickness, etc.) are as described earlier, and thus are not repeated.

<Constitution of Protective Sheet>

The protective sheet disclosed herein typically has a PSA layer on a substrate layer (support substrate or simply a “substrate”; the same applies hereinafter). FIG. 1 shows a cross-sectional structure of the protective sheet according to an embodiment. Protective sheet 10 comprises a PSA layer 2 provided on the first face 1A of a substrate-layer sheet 1. When used, it is applied to an adherend (article to be protected) over the face 2A of PSA layer 2. The back face 1B (on the reverse side of the that face 1A) of substrate layer 1 is also the back face of protective sheet 10, forming the outer surface of protective sheet 10. Prior to use (i.e. before applied to the adherend), protective sheet 10 can be in a form where the face 2A (adhesive face, i.e. the bonding surface to the adherend) of PSA layer 2 is protected with a release liner (not shown in the drawing) having a release face at least on the PSA layer side. Alternatively, protective sheet 10 may be in a form where, with the second surface (back face) 1B of substrate layer 1 being a release face, protective sheet 10 is wound in a roll so that the back face comes in contact with the PSA layer 2 to protect the surface (adhesive face) 2A. The protective sheet may have a PSA layer on each face of the substrate layer.

As the release liner, commonly-used release paper and the like can be used without particular limitations. For instance, a release liner having a release layer on a surface of a liner substrate such as plastic film and paper, a release liner formed from a Low-adhesive material such as fluorinated polymer (polytetrafluoroethylene, etc.) and polyolefinic resin, and the like can be used. The release layer can be formed by subjecting the liner substrate to surface treatment with various release agents including silicone-based, long-chain alkyl-based, and fluorinated kinds as well as molybdenum sulfide.

The protective sheet disclosed herein is not particularly limited in width. For instance, by using a protective sheet having a width of about 1 m or greater or even about 1.5 m or greater, a Low-E glass plate having a relatively large surface area can be efficiently protected. In some preferable embodiments, the protective sheet has a width of about 2 m or greater. With such a broad protective sheet, a lane Low-E glass plate can be protected with a single sheet or a few sheets. For protecting the Low-E glass plate, it is preferable to use a protective sheet having a width of, for instance, about 2.5 m or greater, or even about 2.6 m or greater. The protective sheet's width can be greater than 2.6 m (e.g. 3 m or greater, or even about 3.3 m or greater). The maximum width of the protective sheet is not particularly limited. From the standpoint of the productivity, handling properties, etc., it is suitably about 5 m or less, for instance, possibly about 4 m or less.

The protective sheet disclosed herein can be specified by the plane (sheet face) having a long side and a short side. The long side is defined longer than the short side and the short side is defined shorter than the long side. For instance, the short side may orthogonally intersect the long side. The protective sheet's length direction coincides with the long side and the width direction orthogonally intersects the length direction. Accordingly, as used herein, the “width” is defined as the length (distance) in the direction orthogonal to the length direction. Long-length, belt-like and oblong protective sheets are typical examples of the protective sheet disclosed herein. While the long side extends almost linearly, the short side is not limited to a straight line and can be a curve, zigzag, etc. For instance, in a long protective sheet, the length (distance in the length direction) is equal to or greater than the width.

The thickness of the protective sheet disclosed herein is not particularly limited. From the standpoint of the handling properties, the lightness of weight, etc., it is suitably about 1000 μm or less (typically about 300 μm or less, e.g. about 150 μm or less). In some embodiments, the thickness of the protective sheet is preferably about 120 μm or less, more preferably about 100 μm or less, yet more preferably about 75 μm or less, or possibly, for instance, less than 60 μm. The thickness of the protective sheet can be typically grater than 20 m, preferably greater than 30 μm, or more preferably greater than 40 μm, for instance, greater than 45 μm.

As used herein, the thickness of the protective sheet includes the thicknesses of the PSA layer and the substrate layer, but excludes the thickness of the release liner.

<PSA Layer>

The type of PSA forming the PSA layer disclosed herein is not particularly limited. The PSA layer may be formed from a PSA composition comprising, as the base polymer (the primary component among the polymers, i.e. a component accounting for 50% by weight or more), one, two or more species selected among various polymers (polymers as adhesive components or adhesive polymers), such as acrylic, polyester-based, urethane-based, polyether-based, rubber-based, silicone-based, polyamide-based, and fluorinated polymers. The art disclosed herein can be preferably made, for instance, as a protective sheet comprising an acrylic PSA layer or a rubber-based PSA layer.

The “acrylic PSA layer” here refers to a PSA layer comprising an acrylic polymer as the base polymer. Similarly, the “rubber-based PSA layer” refers to a PSA layer comprising a rubber-based polymer as the base polymer. The “acrylic polymer” refer to a polymer whose primary monomer (the primary component among the monomers, i.e. a component that accounts for 50% by weight or more of the total amount of the monomers forming the acrylic polymer) is a monomer having at least one (meth)acryloyl group per molecule. Such a monomer may be referred to as an “acrylic monomer” hereinafter. As used herein, the “(meth)acryloyl group” comprehensively refers to acryloyl group and methacryloyl group. Similarly, the “(meth)acrylate” comprehensively refers to acrylate and methacrylate.

(Acrylic Polymer)

A preferable example of the acrylic polymer is a polymer of a starting monomer mixture that comprises an alkyl (meth)acrylate (or a monomer A hereinafter) and may further comprise another monomer (or a monomer B hereinafter) that is copolymerizable with the alkyl (meth)acrylate. The acrylic polymer typically has a monomer unit composition corresponding to the monomer composition of the starting monomer mixture.

A preferable monomer A is an alkyl(meth)acrylate represented by the next general formula (1):

CH₂═C(R¹)COOR²  (1)

Here, R¹ in the formula (1) is a hydrogen atom or a methyl group. R² is an alkyl group having 1 to 20 carbon atoms. Hereinafter, such a range of the number of carbon atoms may be indicated as “C₁₋₂₀”. From the standpoint of the polymerization reactivity, polymerization stability, etc., an alkyl (meth)acrylate wherein R² is a C₁₋₁₆ alkyl group is preferable, and an alkyl (meth)acrylate wherein R² is a C₁₋₁₂ (typically C₁₋₁₀, e.g. C₁₋₈) alkyl group is more preferable.

Examples of an alkyl (meth)acrylate with R² being a C₁₋₂₀ alkyl group include methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate, n-butyl (meth)acrylate, isobutyl(methtacrylate, s-butyl(methatylate, t-butyl(meth)acrylate, pentyl (meth)acrylate, isopentyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, n-octyl (meth)acrylate, isooctyl (meth)acrylate, n-nonyl (meth)acrylate, isononyl (meth)acrylate, n-decyl (meth)acrylate, isodecyl (meth)acrylate, undecyl (meth)acrylate, lauryl (meth)acrylate, tridecyl(meth)acrylate, tetradecyl(meth)acrylate, pentadecyl (meth)acrylate, hexadecyl (meth)acrylate, heptadecyl (meth)acrylate, octadecyl (meth)acrylate, nonadecyl (meth)acrylate, eicosyl (meth)acrylate, etc. These alkyl (meth)acrylates can be used solely as one species or in a combination of two or more species.

The at disclosed herein can be preferably implemented in an embodiment where the alkyl acrylate as the monomer A accounts for about 50% by weight or more (more preferably about 75% by weight or more, yet more preferably about 90% by weight or more, e.g. about 95% by weight or more) of the total monomer content. As the alkyl acrylate, an alkyl acrylate with R² in the formula (1) being a C₁₋₂₀ alkyl group is preferable and an alkyl acrylate with R² being a C₁₋₁₂ (more preferably C₁₋₁₀, particularly preferably C₁₋₈) alkyl group is more preferable. The art disclosed herein can also be preferably implemented in an embodiment where the alkyl acrylate has a C₂₋₈ (typically C₁₋₈) alkyl group for R² in the formula (1). For the alkyl acrylate, solely one species or a combination of two or more species can be used. When two or more species of alkyl acrylate are used, to adjust the acrylic polymer's Tg to the most adequate range, etc., an alkyl acrylate A1 with R² being C₄₋₂₀ (more preferably C₄₋₁₀, or yet more preferably C₁₋₈) alkyl group and an alkyl acrylate A2 with R² being a C₁₋₃ (more preferably C₁₋₂, e.g. C₂) alkyl group can be used together. In this embodiment, the alkyl acrylate A1 to alkyl acrylate A2 weight ratio (A1:A2) is not particularly limited. For instance, it is about 5:95 to 95:5, or suitably about 10:90 to 90:10, for instance, about 15:85 to 85:15.

In some preferable embodiments, the monomers include one, two or more species of alkyl methacrylate as the monomer A. With the use of the alkyl methacrylate, the base polymer can be preferably designed so as to achieve desirable adhesive properties. As the alkyl methacylate, an alkyl methacrylate with R² in the formula (1) being a C₁₋₁₀ alkyl group is preferable and an alkyl methacrylate with R² being a C₁₋₄ (more preferably C₁ or C₂₋₄) alkyl group is more preferable. The alkyl methacrylate can be preferably used in combination with an alkyl acrylate. When an alkyl methacrylate and an alkyl acrylate are used together, with one, two or more species of alkyl methacrylate (e.g. C₂₋₄ alkyl methacrylate) having a weight C_(AM) and one, two or more species of alkyl acrylate having a weight C_(AA), their ratio (C_(AM):C_(AA)) is not particularly limited. In some embodiments, it is about 1:9 to 9:1, suitably about 2:8 to 8:2, preferably about 3:7 to 7:3, or more preferably about 4:6 to 6:4. In other embodiments, the ratio of the weight C_(AM) of the alkyl methacrylate (e.g. C₁ alkyl methacrylate, i.e. methyl methacrylate (MMA)) in the total amount (C_(AM)+C_(AA)) of the alkyl (meth)acrylate is about 30% by weight or lower, suitably about 20% by weight or lower, preferably about 10% by weight or lower, or more preferably about 7% by weight or lower. On the other hand, the lower limit is, for instance, about 0.1% by weight or higher, suitably about 1% by weight or higher, or preferably about 2% by weight or higher (e.g. about 3% by weight or higher).

The art disclosed herein can be implemented in an embodiment where the monomers are essentially free of an alkyl methacrylate as the monomer A. In an embodiment using an alkyl methacrylate, it can be implemented, for instance, in an embodiment free of a C₁₋₃ alkyl methacrylate (typically MMA).

In another preferable embodiment, the acrylic polymer is a polymer of a starting monomer mixture that comprises an alkyl acrylate (or a monomer m_(A), hereinafter) having 4 to 9 alkyl carbon atoms and may further comprise other monomer(s) as necessary. The acrylic polymer can be synthesized by polymerizing a starting monomer mixture having the corresponding composition (monomer composition) by a known method.

Non-limiting examples of monomer m_(A) include n-butyl acrylate (BA), n-hexyl acrylate, 2-ethylhexyl acrylate (2EHA), n-octyl acrylate, n-nonyl acrylate and isononyl acrylate (iNA). A preferable alkyl acrylate includes a —(CH₂)₃— structure in the alkyl group and a more preferable alkyl acrylate includes a —(CH₂)₄— structure in the alkyl group. Favorable examples of monomer m_(A) include 2EHA, BA and iNA. For the monomer m_(A), solely one species or a combination of two or more species can be used.

The amount of monomer m_(A) used typically accounts for 40% by weight or more of the starting monomers used in the synthesis of acrylic polymer. From the standpoint of the flexibility and enhanced Low-temperature properties of the PSA layer comprising the acrylic polymer, it is advantageous that the monomer composition includes at least 40% monomer m_(A) by weight. From such a standpoint, the ratio of monomer m_(A) is preferably 45% by weight or higher, or possibly 50% by weight or higher (e.g. above 50% by weight). When the monomer composition includes 99.9% or less monomer m_(A) by weight, the PSA layer comprising the acrylic polymer is likely to have suitable cohesion. From such a standpoint, the ratio of monomer m_(A) is preferably 95% by weight or lower, more preferably 9) % by weight or lower, or possibly 85% by weight or lower. In some embodiments, the ratio of monomer m_(A) can be below 80% by weight or even below 70% by weight (e.g. 65% by weight or lower).

The acrylic polymer in the art disclosed herein may have a monomer composition comprising a carboxy group-containing monomer (or a monomer m_(B), hereinafter) as the monomer B. In other words, a monomer m_(B) may be copolymerized in the acrylic polymer. The monomer m_(B) may be useful in introducing crosslinking points into the acrylic polymer and increasing the cohesive strength of the PSA layer comprising the acrylic polymer. The monomer m_(B) may help enhance the anti-PSA-residue properties by increasing the tightness of adhesion (anchoring) between the acrylic polymer-containing PSA layer and the substrate layer. Examples of the carboxy group-containing monomer include ethylenically unsaturated monocarboxylic acids such as acrylic acid, methacrylic acid, crotonic acid, isocrotonic acid, carboxyethyl (meth)acrylate, carboxypentyl (meth)acrylate and 1-[2-(methacryloyloxy)ethyl] succinate; ethylenically unsaturated dicarboxylic acids such as maleic acid, fumaric acid, itaconic acid and citraconic acid, and anhydrides thereof (e.g. maleic anhydride, itaconic anhydride, etc.). These carboxy group-containing monomers can be used singly as one species or in a combination of two species.

When using a monomer m_(B), the ratio of monomer m_(B) in the monomer composition is not particularly limited. The ratio of monomer m_(B) can be, for instance, 0.05% by weight or higher, or suitably 0.1% by weight or higher. From the standpoint of the polymerization stability and dispersion stability, it is preferably 0.5% by weight or higher, or more preferably 1% by weight or higher. From the standpoint of inhibiting an excessive increase in peel strength (adhesive strength), the ratio of monomer m_(B) is suitably about 20% by weight or lower (preferably about 10% by weight or lower, typically about 7% by weight or lower), more preferably about 5% by weight or lower, or yet more preferably about 4% by weight or lower (e.g. 3% by weight or lower). From the standpoint of inhibiting erosion of the Low-E glass plate as the object to be protected, it is preferable to limit the amount of carboxy group-containing monomer used.

In the acrylic polymer in the art disclosed herein, for purposes such as adjusting the glass transition temperature (Tg) of the acrylic polymer, an alkyl (meth)acylate (or a monomer m_(C), hereinafter) may be copolymerized as the monomer A, the alkyl(meth)acrylate having 4 to 20 alkyl carbon atoms and having a homopolymer Tg of −50° C. or higher. Here, a monomer belonging to the monomer m_(A) is not categorized as a monomer me. For the monomer m_(C), solely one species or a combination of two or more species can be used. A preferable monomer m_(C) has a homopolymer Tg in the range between −40° C. and +60° C. and a more preferable monomer me in the range between −30° C. and +40° C. (e.g. between −20° C. and +30° C.). Non-limiting examples of a monomer m_(C) that can be preferably used include n-butyl methacrylate (BMA), 2-ethylhexyl methacrylate and lauryl acrylate.

When using a monomer me, the ratio of monomer me in the monomer composition is not particularly limited. The ratio of monomer me can be, for instance, 1% by weight or higher, 5% by weight or higher, 10% by weight or higher, or even 15% by weight or higher. In an embodiment, from the standpoint of obtaining greater effect of monomer m_(C), the ratio of monomer me in the monomer composition can also be 20% by weight or higher, 25% by weight or higher, 30% by weight or higher, or even 35% by weight or higher (e.g. 40% by weight or higher). The ratio of monomer n in the monomer composition can be below 60% by weight. From the standpoint of the flexibility and enhanced Low-temperature properties, it is suitably about 55% by weight or lower (typically about 50% by weight or lower, e.g. about 45% by weight or lower). In some embodiments, the ratio of monomer m_(C) can be below 30% by weight, below 20% by weight or even below 10% by weight (e.g. below 5% by weight, or even below 1% by weight).

In the acrylic polymer in the ail disclosed herein, as necessary, other monomer(s)(monomer m_(D)) can be copolymerized as the monomer A besides monomers m_(A), m_(B) and m_(C). As the monomer m_(D), among various monomers copolymerizable with monomer m_(A), solely one species or a combination of two or move species can be used.

As the monomer m_(D), for instance, it is possible to use an alkyl (meth)acrylate (monomer m_(D)) represented by the formula (1) shown earlier (while excluding any species considered a monomer m_(A) or monomer m_(C)). Specific examples of the alkyl (meth)acrylate that can be used as monomer m_(D), include methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate and the like. For the monomer mot, solely one species or a combination of two or more species can be used.

Examples of compounds that can be used as the monomer m_(D) may include a functional group-containing monomer (monomer B) such as those described below. These functional group-containing monomers may be useful for introducing crosslinking points into the acrylic polymer or for increasing the cohesive strength of the acrylic polymer:

Hydroxy group-containing monomers: e.g. hydroxyalkyl(meth)acrylates such as 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl(meth)acrylate, 3-hydroxypropyl (meth)acrylate, 2-hydroxybutyl(meth)acrylate, 4-hydroxybutyl (meth)acrylate, 6-hydroxyhexyl(meth)acrylate, 8-hydroxyoctyl (meth)acrylate, 10-hydroxydecyl (meth)acrylate, 12-hydroxyaryl (meth)acrylate and (4-hydroxymethylcyclohexyl)methyl acrylate; unsaturated alcohols such as vinyl alcohol and allyl alcohol.

Amide group-containing monomers: e.g. (meth)acrylamide, N,N-dimethyl (meth)acrylamide, N,N-diethyl (meth)acrylamide. N,N-dimethylaminopropyl (meth)acrylamide, N-butyl (meth)acrylamide, N-methylol (meth)acrylamide. N-methylolpropane (meth)acrylamide. N-methoxymethyl (meth)acrylamide, N-butoxymethyl (meth)acrylamide and diacetone (meth)acrylamide:

imide group-containing monomers: e.g. N-isopropylmaleimide, N-cyclohexylmaleimide, itaconimide:

Amino group-containing monomers: e.g. aminoethyl (meth)acrylate, N,N-dimethylaminoethyl(meth)acrylate, N,N-dimethylaminopropyl (meth)acrylate, t-butylaminoethyl (meth)acrylate:

Epoxy group-containing monomers: e.g. glycidyl (meth)acrylate, methylglycidyl (meth)acrylate, allyl glycidyl ether:

Cyano group-containing monomers: e.g. acrylonitile, methacrylonitrile;

Keto group-containing monomers: e.g. diacetone (meth)acrylamide, diacetone (meth)acrylate, vinyl methyl ketone, vinyl ethyl ketone, ally acetoacetate, vinyl acetoacetate;

Monomers having nitrogen atom-containing rings: e.g. N-vinyl-2-pyrolidone. N-methylvinylpyrolidone, N-vinylpyridine, N-vinylpiperidone, N-vinylpyrimidine, N-vinylpiperazine, N-vinylpyrazine, N-vinylpyrrole, N-vinylimidazole, N-vinyloxazole, N-vinylmorphline, N-vinylcapolactam, N-(meth)acryloyl morpholine, N-(meth)acryloylpyrrolidone;

Alkoxysilyl group-containing monomers: e.g. (3-(meth)acryloxypropyl)trimethoxysilane, (3-(meth)acryloxypropyl)triethoxysilane, (3-(meth)acryloxypropyl)methyldimethoxysilane, (3-(meth)acryloxypropyl)methyldiethoxysilane.

Other examples of the compound that can be used as the monomer m_(D) include vinyl ester-based monomers such as vinyl acetate and vinyl propionate; aromatic vinyl compounds such as styrene, substituted styrenes (α-methylstyrene, etc.) and vinyltoluene; non-aromatic ring-containing (meth)acrylates such as cyclohexyl (meth)acrylate, t-butylcyclohexyl (meth)acrylate, cyclopentyl di(meth)acrylate and isobornyl (meth)acrylate; aromatic ring-containing (meth)acrylates such as aryl (meth)acrylates (e.g. phenyl (meth)acrylate, benzyl(meth)acrylate), aryloxyalkyl (meth)acrylate (e.g. phenoxyethyl (meth)acrylate), arylalkyl (meth)acylate (e.g. benzyl (meth)acrylate); olefinic monomers such as ethylene, propylene, isoprene, butadiene and isobutylene; chlorine-containing monomers such as vinyl chloride and vinylidene chloride; isocyanate group-containing monomers such as 2. (meth)acryloxyethylisocyanate; alkoxy group-containing monomers such as methoxymethyl (meth)acrylate and ethoxyethyl (meth)acrylate; vinyl ether-based monomers such as methyl vinyl ether, ethyl vinyl ether and isobutyl vinyl ether.

Yet other examples of the compound that can be used as the monomer m_(D) include polyfunctional monomers. Specific examples of polyfunctional monomers include compounds having two or more (meth)acryloyl groups per molecule such as 1,6-hexanediol di(meth)acylate, ethylene glycol di(meth)acrylate, pentaerythritol di(meth)acrylate, trimethylolpropane di(meth)acrylate, dipentaerythritol hexa(meth)acrylate and methylene bisacrylamide. When using such a polyfunctional monomer, its amount used is not particularly limited. It is suitably 2% by weight or less (more preferably 1% by weight or less) of the total monomer content.

The monomer m_(D) is used in an amount of typically no more than 40% by weight of the monomer composition, preferably no more than 20% by weight, or more preferably no more than 10% by weight. The monomer nm may not be used. The art disclosed herein can be preferably practiced in an embodiment where the amount of monomer m_(D) used is 0% or more and below 5% by weight of the monomer composition. Here, that the amount of monomer m_(D) used is 0% by weight means that no monomer m is used at least intentionally.

The ratio of monomer A (alkyl (meth)acrylate) in the total monomer content can be, but is not particularly limited to, for instance, about 50% by weight or grater it is suitably about 60% by weight or greater, preferably about 70% by weight or greater, more preferably about 80% by weight or greater, or yet more preferably about 85% by weight or greater. With the inclusion of the monomer A in a prescribed amount, a protective sheet having desirable adhesive properties can be favorably obtained. The art disclosed herein can be preferably implemented, for instance, in an embodiment where the monomer A content in the total monomer content is about 90% by weight or greater. In an embodiment, the monomer A content can be about 95% by weight or greater, or even about 97% by weight or greater. The PSA composition comprising such an acrylic polymer as the base polymer can be advantageous from the standpoint of the weatherability of the PSA layer formed therefrom (and also the protective sheet having the PSA layer). In an embodiment using a monomer A and a monomer B together, from the standpoint of suitably obtaining the effects of the monomer B, the monomer A content in the total monomer content can be, for instance, 99.9% by weight or less; it is preferably 99.5% by weight or less, more preferably 99% by weight or less, or about 97% by weight or less (e.g. 95% by weight or less).

When an aforementioned functional group-containing monomer is copolymerized in the acrylic polymer, the ratio of the functional group-containing monomer to all the monomers forming the acrylic polymer is preferably about 0.1% by weight or higher (typically about 0.5% by weight or higher, e.g. about 1% by weight or higher), and preferably about 40% by weight or lower (typically about 30% by weight or lower, e.g. about 20% by weight or lower). When a hydroxy group-containing monomer is copolymerized with the acrylic monomer, from the standpoint of obtaining desirable cohesive strength, the ratio of hydroxy group-containing monomers to the total monomer content is suitably about 0.001% by weight or higher (typically about 0.01% by weight or higher, e.g. about 0.1% by weight or higher), preferably about 1% by weight or higher, or more preferably about 3% by weight or higher; it is preferably about 10% by weight or lower (typically about 7% by weight or lower, e.g. about 5% by weight or lower).

(Rubber-Based Polymer)

In another preferable embodiment, the PSA layer can be a rubber-based PSA layer. Examples of the base polymer include natural rubber styrene-butadiene rubber (SBR); polyisoprene; butene-based polymer comprising a butene (1-butene or cis- or trans-2-butene) and/or 2-methylpropene (isobutylene) as the primary monomer(s); A-B-A block copolymer rubber and a hydrogenation product thereof, e.g. styrene-butadiene-styrene block copolymer rubber (SBS), styrene-isoprene-styrene block copolymer (SIS), styrene-isobutylene-styrene block copolymer rubber (SIBS), styrene-vinyl-isoprene-styrene block copolymers (SVIS), hydrogenated SBS (stryene-ethylene/butylene-styrene block copolymer (SEBS)), and hydrogenated SIS (styrene-ethylene-propylene-styrene block copolymers (SEPS)). These rubber-based polymers can be used singly as one species or in a combination of two or more species.

(Tg of Base Polymer)

The Tg value of the PSA layer's base polymer (an acrylic polymer in case of an acrylic PSA layer being used) is not particularly limited in Tg. The Tg of the base polymer can be, for instance, about 0° C. or lower. In a preamble embodiment, the base polymer of the PSA layer has a Tg of about −5° C. or lower. According to a base polymer having such a Tg, a PSA layer that tightly adheres to adherend can be favorably formed. In an embodiment where the base polymer has a Tg of about −15° C. or lower (more preferably about −20° C. or lower, e.g. about −25° C. or lower), greater effects can be obtained. In other preferable embodiments, from the standpoint of the adhesion to adherends, the base polymer of the PSA layer has a Tg of about −35° C. or lower, more preferably about −40° C. or lower, or yet more preferably about −45° C. or lower (e.g. below −50° C., even about −52° C. or lower, or about −55° C. or lower). The Tg of the base polymer is suitably −70° C. or higher. From the standpoint of the cohesion of the PSA, etc., it is preferably about −65° C. or higher, more preferably −60° C. or higher, yet more preferably about −55° C. or higher (e.g. about −50° C. or higher), or possibly even about −35° C. or higher. The base polymer's Tg can be adjusted by suitably changing the monomer composition (i.e. the monomer species used in the synthesis of the polymer and their ratio).

In the present description, the Tg of a polymer refers to the value determined by the Fox equation based on the Tg values of homopolymers of the respective monomers forming the polymer and the weight fractions (copolymerization ratio by weight) of the monomers. As shown below, the Fox equation is a relational expression between the Tg of a copolymer and glass transition temperatures Tgi of homopolymers of the respective monomers constituting the copolymer.

1/Tg=Σ(Wi/Tgi)

In the Fox equation, Tg represents the glass transition temperature (unit: K) of the copolymer, Wi the weight fraction (copolymerization ratio by weight) of a monomer i in the copolymer, and Tgi the glass transition temperature (unit: K) of homopolymer of the monomer i.

For the glass transition temperatures of homopolymers used for determining the Tg, the values found in known documents are used. For instance, with respect to the monomers listed below, for the glass transition temperatures of their homopolymers, the following values are used:

2-ethylhexyl acrylate −70° C. n-hexyl acrylate −65° C. n-octylacrylate −65° C. isononyl acrylate −60° C. n-nonyl acrylate −58° C. n-butyl acrylate −55° C. ethyl −20° C. lauryl acrylate  0° C. 2-ethylhexyl methacrylate −10° C. methyl acrylate  8° C. n-butyl methacrylate  20° C. methyl methacrylate 105° C. acrylic acid 106° C. methacrylic acid 228° C. vinyl acetate  32° C. styrene 100° C.

With respect to the Tg values of homopolymers other than the examples listed above, the values given in Polymer Handbook (3rd edition, John Wiley & Sons, Inc., Year 1989) are used. With respect to a monomer for which two or more values an listed in the Polymer Handbook, the highest value is used. When no values are given in the Polymer Handbook, values obtained by the measurement method described in Japanese Patent Application Publication No. 2007-51271 are used.

((Synthesis of Base Polymer)

The method for obtaining the base polymer (e.g. an acrylic polymer) is not particularly limited. Known polymerization methods can be suitably employed, such as solution polymerization, emulsion polymerization, bulk polymerization, and suspension polymerization. Alternatively, it is also possible to employ photopolymerization involving irradiation of light such as UV (typically carried out in the presence of a photopolymerization initiator) and active energy ray irradiation polymerization such as radiation polymerization involving irradiation of radioactive rays such as P rays and y rays. In some preferable embodiments, the base polymer (e.g. acrylic polymer) is typically obtained by emulsion polymerization of a starting monomer mixture having an aforementioned composition. As the monomer supply method in, for instance, emulsion polymerization, a suitable method can be employed among the all-at-once method where all the starting monomer mixture is supplied in one portion, gradual supply method, portion-wise supply method, etc. An emulsion of some or all of the monomers pre-mixed with water and a surfactant can be supplied to the polymerization vessel.

The polymerization temperature can be suitably selected in accordance with the monomer species, the solvent species, and the polymerization initiator species used, etc. The polymerization temperature is suitably about 20° C. or higher, preferably about 40° C. or higher, more preferably about 50° C. or higher; it can also be about 60° C. or higher, about 65° C. or higher, or even about 70° C. or higher. The polymerization temperature is usually suitably about 170° C. or lower (typically about 140° C. or lower), or preferably about 95° C. or lower (e.g. about 85° C. or lower). In emulsion polymerization, the polymerization temperature is preferably about 95° C. or lower (e.g. about 85° C. or lower).

The polymerization solvent (solvent used in solution polymerization) can be suitably selected among heretofore known organic solvents. Preferable examples include aromatic compounds (typically aromatic hydrocarbons) such as toluene, acetates such as ethyl acetate, aliphatic and alicyclic hydrocarbons such as hexane and cyclohexane.

Examples of the polymerization initiator include, but not limited to, azo-based initiators, peroxide-based initiators and redox-based initiators by the combination of a peroxide and a reducing agent. For the polymerization initiator, solely one species or a combination of two or more species can be used.

Examples of azo-based initiators include 2,2′-azobisisobutyronitrile, 2,2′-azobis[N-(2-carboxyethyl)-2-methylpropionamidine] hydrate, 2,2′-azobis(2-methylpropionamidine)disulfate salt, 2,2′-azobis(2-methylpropionamidine) dihydrochloride, 2,2′-azobis[2-(5-methyl-2-imidazolin-2-yl)propane] dihydrochloride and 2,2′-azobis(N,N′-dimethylene isobutylamidine) dihydrochloride.

Examples of the peroxide-based initiator include persulfates such as potassium persulfate and ammonium persulfate; benzoyl peroxide, t-butyl hydroperoxide, di-t-butyl peroxide, dicumyl peroxide, dilauroyl peroxide, di-n-octanoyl peroxide, di(4-methylbenzoyl) peroxide, t-butyl peroxybenzoate, t-butyl peroxyisobutyrate, t-hexyl peroxypivalate, t-butyl peroxypivalate, di(2-ethylhexyl) peroxydicarbonate, di(4-t-butylcyclohexyl) peroxydicarbonate, di-sec-butyl peroxydicarbonate, t-butyl peroxyneodecanoate, 1,1,3,3-tetramethyl butylperoxy-2-ethylhexanoate, 1,1-bis(t-butylperoxy)-3,3,5-trimethylcyclohexane, 1,1-bis(t-butylperoxy)cyclododecane, 1,1-bis(t-hexylperoxy)cyclohexane and hydrogen peroxide.

Examples of the redox-based initiator include a combination of a peroxide and ascorbic acid (combination of hydrogen peroxide and ascorbic acid, etc.), a combination of a peroxide and an iron(II) salt (combination of hydrogen peroxide and an iron(II) salt, etc.), and a combination of a persulfate salt and sodium hydrogen sulfite.

The polymerization initiator can be used in an amount suitably selected in accordance with the type of initiator, monomer species (monomer composition), polymerization conditions, etc. The amount of polymerization initiator used is, for instance, about 0.0005 part to 1 part by weight to 100 parts by weight of the starting monomers: and it is suitably, for instance, in the range between about 0.001 part and 0.5 part by weight; preferably in the range between 0.002 part and 0.3 part by weight; and more preferably in the range between 0.005 part and 0.1 part by weight.

In the emulsion polymerization, as necessary, various heretofore known chain transfer agents (which can be considered also as a molecular weight-adjusting agent or polymerization degree-adjusting agent) can be used. For the chain transfer agent, solely one species or a combination of two or more species can be used. As the chain transfer agent, mercaptans can be preferably used, such as n-dodecyl mercaptan, t-dodecyl mercaptan, glycidyl mercaptan, 2-mercaptoethanol, mercaptoacetic acid, thioglycolic acid, 2-ethylhexyl thioglycolate and 2,3-dimercapto-1-propanol. When using a chain transfer agent, its amount used to 100 parts by weight of the total monomer content is, for instance, possibly about 0.01 to 1 part by weight, preferably 0.02 to 0.1 part by weight, or more preferably 0.03 to 0.07 part by weight. The art disclosed herein can be preferably practiced in an embodiment without use of a chain transfer agent.

The surfactant (emulsifier) used in emulsion polymerization is not particularly limited. Commonly-known anionic surfactants, nonionic surfactants and the like can be used. A surfactant having a radically polymerizable functional group can also be used. Hereinafter, the surfactant having a radically polymerizable functional group is referred to as a reactive (polymerizing) surfactant. In contrast to this, a general surfactant free of a radically polymerizable functional group may be referred to as a non-reactive (non-polymerizing) surfactant. For the surfactant, solely one species or a combination of two or more species can be used.

Examples of the non-reactive surfactant include anionic emulsifiers such as sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecyl benzenesulfonate, sodium polyoxyethylene lauryl sulfate, sodium polyoxyethylene alkyl ether sulfates, ammonium polyoxyethylene alkyl phenyl ether sulfates, sodium polyoxyethylene alkyl phenyl ether sulfates, and sodium polyoxyethylene alkyl sulfosuccinates, and non-ionic emulsifiers such as polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene aliphatic acid esters, and polyoxyethylene-polyoxypropylene block polymers.

The reactive surfactant is not particularly limited as far as it has a radically polymerizable functional group. For instance, the reactive surfactant may have a structure such that a radically polymerizable functional group is incorporated in an aforementioned anionic surfactant or nonionic surfactant. Examples of the radically polymerizable functional group include vinyl group, propenyl group, isopropenyl group, vinyl ether group (vinyloxy group), and allyl ether group (allyloxy group). The concept of propenyl group referred to herein encompasses 1-propenyl group (CH₃—CH═CH—) and 2-propenyl group (CH₂═CH—CH₂— which may be called allyl group).

Examples of an anionic reactive surfactant include polyoxyethylene (allyloxymethyl) alkyl ether sulfates (e.g. ammonium salts), polyoxyethylene nonyl propenyl phenyl ether sulfates (e.g. ammonium salts), alkyl allyl sulfosuccinates (e.g. sodium salts), methacryloxy polyoxypropylene sulfuric acid ester salts (e.g. sodium salts), and polyoxyalkylene alkenyl ether sulfates (e.g. an ammonium salt having an isopropenyl group as the terminal alkenyl group). When the anionic reactive surfactant is forming a salt, the salt can be, for instance, a metal salt such as sodium salt or a non-metal salt such as ammonium salt and amine salt.

Examples of a nonionic reactive surfactant include polyoxyethylene nonyl propenyl phenyl ether.

Although no particular limitations are imposed, in some embodiments, a reactive surfactant having an oxyethylene chain can be preferably used. The oxyethylene chain refers to a structure of repeating oxyethylene units, that is, a structural moiety represented by —(C₂H₄O)_(n)—, with n indicating the number of repeats of the oxyethylene unit. For instance, in a preferable reactive surfactant, the number of repeats, n, is about 5 to 30 (e.g. 8 to 25).

From the standpoint of the polymerization stability during the emulsion polymerization, in some embodiments, it is preferable to use a reactive surfactant having a propenyl group. A preferable reactive surfactant has a propenyl group and also an oxyethylene chain.

From the standpoint of the emulsifying ability, etc., in some embodiments, an anionic reactive surfactant (e.g. an anionic reactive surfactant having an oxyethylene chain) can be preferably used. When the anionic reactive surfactant is in a salt form, as the salt, a non-metal salt is preferable. In particular, an ammonium salt is preferable.

When using a nonionic reactive surfactant, more favorable results can be obtained by the combined use with other surfactant(s), such as an anionic reactive surfactant, anionic non-reactive surfactant and nonionic non-reactive surfactant.

By carrying out emulsion polymerization of the starting monomer mixture in the presence of a reactive surfactant having a radically polymerizable functional group, the reactive surfactant may undergo a reaction to be incorporated into the base polymer (e.g. acrylic polymer). The reactive surfactant incorporated in the acrylic polymer is less likely to bleed out to the PSA layer surface because its move within the PSA layer is limited. Accordingly, the use of the reactive surfactant can reduce bleed-out of a low molecular weight compound to the PSA layer surface. This is preferable from the standpoint of the Low-contaminating properties. From the standpoint of obtaining greater Low-contaminating properties, it is preferable to apply an embodiment using solely a reactive surfactant as the surfactant for emulsion polymerization.

The amount of surfactant is preferably about 0.1 part by weight or greater (e.g. about 0.5 part by weight or greater) to 100 parts by weight of the total monomer content. The amount of surfactant is suitably about 10 parts by weight or less (e.g. about 5 parts by weight or less) or possibly even about 4 parts by weight or less to 100 parts by weight of the total monomer content.

The PSA layer disclosed herein may comprise about 50% or more base polymer by weight. The base polymer content in the PSA layer is possibly about 75% by weight or higher, or suitably about 85% by weight or higher. With the PSA having at least the prescribed percentage of base polymer, contamination of the protected article is readily prevented or inhibited; and the adhesive properties also tend to be highly stable to aging. In some preferable embodiments, the base polymer content in the PSA layer is about 90% by weight or higher, more preferably about 95% by weight or higher, yet more preferably about 97% by weight or higher, or possibly even 98% by weight or higher (e.g. about 99% by weight or higher). The maximum base polymer content of the PSA layer is 100% by weight. To obtain projected properties (e.g. alteration resistance, tightness of adhesion, etc.), it can be 99.5% by weight or lower, 98.5% by weight or lower, or even 97.5% by weight or lower.

The PSA layer of the PSA sheet disclosed herein can be formed from various forms of PSA compositions. Examples of the forms of PSA compositions include a solvent-based PSA composition containing the PSA (adhesive component(s)) in an organic solvent, a water-dispersed PSA composition containing at least part of the PSA dispersed in an aqueous solvent, an active energy ray-curable PSA composition formulated so as to cure with active energy rays such as UV rays and radioactive rays to from PSA, and a hot-melt PSA composition which is applied in the molten state by heating and forms PSA when it cools to near room temperature.

From the standpoint of reducing environmental stress, a water-dispersed PSA composition can be preferably used. A favorable example of the water-dispersed PSA composition is a water-dispersed PSA composition (a water-dispersed acrylic PSA composition, typically an acrylic emulsion PSA composition) comprising an acrylic polymer as the base polymer. The use of water-dispersed PSA composition is also preferable in view of film formation in the Low-E layer. From the standpoint of the adhesive properties, a solvent-based PSA composition is preferable. The hot-melt PSA composition requiring no use of a solvent is advantageous for its excellent handling properties in the production process.

(Crosslinking Agent)

In the art disclosed herein, the PSA composition used to form the PSA layer preferably comprises a crosslinking agent. With the use of crosslinking agent, the surface hardness of the PSA layer can be suitably adjusted. The type of crosslinking agent used is not particularly limited and can be suitably selected from heretofore known crosslinking agents.

Specific examples of the crosslinking agent include oxazoline-based crosslinking agents, aziridine-based crosslinking agents, isocyanate-based crosslinking agents, epoxy-based crosslinking agents, melamine-based crosslinking agents, peroxide-based crosslinking agents, urea-based crosslinking agents, metal alkoxide-based crosslinking agents, metal chelate-based crosslinking agents, metal salt-based crosslinking agents, carbodiimide-based crosslinking agents, hydrazine-based crosslinking agents, amine-based crosslinking agents, and silane coupling agents. These can be used solely as one species or in a combination of two or more species. For instance, it is preferable to use one, two or more species selected from a group consisting of oxazoline-based crosslinking agents, aziridine-based crosslinking agents, isocyanate-based crosslinking agents and epoxy-based crosslinking agents. In particular, oxazoline-based crosslinking agent, isocyanate-based crosslinking agent and epoxy-based crosslinking agent are more preferable. In an embodiment using a water-dispersed PSA composition, a preferable crosslinking agent is soluble or dispersible in water and a particularly preferable crosslinking agent is soluble in water (i.e. water-soluble).

As the oxazoline-based crosslinking agent, a species having one or more oxazoline groups per molecule can be used without particular limitations. In the water-dispersed PSA composition, it is preferable to use a water-soluble or water-dispersible oxazoline-based crosslinking agent.

The oxazoline group can be either 2-oxazoling group, 3-oxazoline group or 4-oxazoline group. Usually, a 2-oxazoline group-containing oxazoline-based crosslinking agent can be preferably used. As the oxazoline-based crosslinking agent, a water-soluble copolymer or a water-dispersed copolymer can be used, which is obtained by copolymerizing an addition-polymerizable oxazoline such as 2-vinyl-2-oxazoline, 2-vinyl-4-methyl-2-oxazoline, 2-vinyl-5-methyl-2-oxazoline, 2-isopropenyl-2-oxazoline 2-isopropenyl-4-methyl-2-oxazoline and 2-isopropenyl-5-ethyl-2-oxazoline with other monomer(s). Examples of a commercial oxazoline-based crosslinking agent include products of Nippon Shokubai Co., Ltd., under trade names EPOCROS WS-500, EPOCROS WS-700, EPOCROS K-2010E, EPOCROS K-2020E and EPOCROS K-2030L.

Examples of the aziridine-based crosslinking agent include trimethylolpropane tris[3-(1-azindinyl)propionate] and trimethylolpropane tris[3-(1-(2-methyl)aziridinylpropionate)]. Examples of commercial aziridine-based crosslinking agent include product names CHEMITITE PZ-33 and CHEMITITE DZ-22E available from Nippon Shokubai Co., Ltd.

As an example of the isocyanate-based crosslinking agent, a bifunctional or higher polyfunctional isocyanate compound can be used. Examples include aromatic isocyanates such as tolylene diisocyanates, xylylene diisocyanate, polymethylene polyphenyl diisocyanate, tris(p-isocyanatophenyl)thiophosphate, and diphenylmethane diisocyanate; alicyclic isocyanates such as isophorone diisocyanate; and aliphatic isocyanates such as hexamethylene diisocyanate. Commercial products include isocyanate adducts such as trimethylolpropane/tolylene diisocyanate trimer adduct (trade name CORONATE L available from Tosoh Corporation), trimethylolpropane/hexamethylene diisocyanate trimer adduct (trade name CORONATE HL available from Tosoh Corporation) and hexamethylene diisocyanate isocyanurate (trade name CORONATE IX available from Tosoh Corporation). In the water-dispersed PSA composition, it is preferable to use a water-soluble or water-dispersible isocyanate-based crosslinking agent. For instance, a water-soluble, water-dispersible or self-emulsifying isocyanate-based crosslinking agent can be preferably used. A so-called blocked isocyanate-based crosslinking agent can be preferably used as an isocyanate-based crosslinking agent.

As the epoxy-based crosslinking agent, a species having two or more epoxy groups per molecule can be used without particular limitations. An epoxy-based crosslinking agent having 3 to 5 epoxy groups per molecule is preferable. In the water-dispersed PSA composition, it is preferable to use a water-soluble or water-dispersible epoxy-based crosslinking agent.

Specific examples of the epoxy-based crosslinking agent include N,N′,N′-tetraglycidyl-m-xylenediamine, 1,3-bis(N,N-diglycidylaminomethyl)cyclohexane, 1,6-hexanediol diglycidyl ether, polyethylene glycol diglycidyl ether, and polyglycerol polyglycidyl ether.

Commercial epoxy-based crosslinking agents include products of Mitsubishi Gas Chemical Co., Inc., under trade names TETRAD-X and TETRAD-C, a product of DIC Corporation under trade name EPICLON CR-5L, a product of Nagase ChemteX Corporation under trade name DENACOL EX-512, and a product of Nissan Chemical Industries, Ltd., under trade name TEPIC-G.

As the carbodiimide-based crosslinking agent, a low or high molecular weight compound having two or more carbodiimide groups can be used. In a water-dispersed PSA composition, it is preferable to use a water-soluble or water-dispensible carbodiimide-based crosslinking agent. Examples of commercial carbodiimide-based crosslinking agents include the CARBODILITE series such as the CARBODILITE V series (aqueous solutions) including CARBODILITE V-02, CARBODILITE V-02-L2, and CARBODILITE V-04; and the CARBODILITE series (aqueous dispersions) including CARBODILITE E-01, CARBODILITE E-02, and CARBODILITE E-04 available from Nisshinbo Holdings, Inc.

The crosslinking agent content (the total amount of crosslinking agent) in the PSA composition disclosed herein is not particularly limited and can be suitably selected in view of the composition and the molecular weight of the base polymer so as to obtain favorable properties after crosslinked. While no particular limitations are imposed, the amount of the crosslinking agent used to 100 parts by weight of the base polymer (typically an acrylic polymer) is, for instance, about 0.01 part by weight or greater, suitably about 0.1 part by weight or greater, or preferably about 1 part by weight or greater (e.g. about 2 parts by weight or greater). From the standpoint of the adhesion, etc., the amount of the crosslinking agent is suitably about 15 parts by weight or less (preferably about 10 parts by weight or less, e.g. about 5 parts by weight or less) to 100 parts by weight of the base polymer. From the standpoint of increasing the tightness of adhesion to adherends, it is preferably about 4 parts by weight or less, more preferably less than 3.5 parts by weight, or yet more preferably less than 3 parts by weight.

(Phosphorous Compound)

The PSA layer disclosed herein is characterized by the inclusion of a phosphorous compound having a P—OR group. According to the phosphorous compound-containing PSA, Low-E layer alteration can be prevented or inhibited not only for the protection period with the protective sheet, but also after its removal. In particular, for protecting a Low-E layer, when the PSA layer of the protective sheet is adhered to the Low-E layer face of the Low-E glass plate, the phosphorous compound in the PSA layer transfers to the Low-E layer surface to react with the tin component of the Low-E layer, thereby forming a film on the Low-E layer. In particular, the film is formed on the outer surface of the Low-E layer or internal to the Low-E layer. The presence of the film can block the entry of an alteration-causing substance and the like from the outside.

In the P—OR group of the phosphorous compound, R is a hydrogen atom or an organic group. The organic group may have an alkyl group, aryl group, alkyl aryl group, or oxyalkylene chain (e.g. oxyethylene chain). The alkyl group can be a linear, branched or alicyclic alkyl group. The number of carbon atoms in the alkyl group is, for instance, 1 to 30, possibly 2 or higher (e.g. 4 or higher); and 20 or lower, preferably 18 or lower, for instance, possibly 15 or lower. The number of carbon atoms in the aryl group is 6 or higher (preferably 8 or higher. e.g. 11 or higher); and possibly 30 or lower (typically 20 or lower, preferably 10 or lower. e.g. 8 or lower). The organic group having an oxyalkylene chain is represented by —(CH₂CH₂)_(n)OR^(a). In the formula, n is an integer between 1 and 30; it can be typically an integer between about 1 and 20, preferably an integer between about 1 and 10, for instance, an integer between about 1 and 8. The number of moles of EO added, n, is preferably an integer between about 1 and 6, or yet more preferably an integer between 1 and 4 (e.g. 2 and 4). R^(a) is a mono-valent organic group (typically hydrocarbon group); for instance, it can be a group selected among an alkyl group, cycloalkyl group, aryl group, alkylaryl group, and arylalkyl group. R^(a) is preferably a linear or branched alkyl group, aryl group or alkylaryl group. R^(a) is an organic group with 1 to 30 carbon atoms, or possibly an organic group with 6 or more (preferably 8 or more, e.g., 11 or more) carbon atoms. In some preferable embodiments. R^(a) can be an organic group with 20 or fewer or preferably 18 or fewer, for instance, 15 or fewer carbon atoms. For the phosphorous compound, solely one species or a combination of two or more species can be used.

The phosphorous compound in the PSA layer can be an inorganic phosphorous compound or an organic phosphorous compound. Examples of the inorganic phosphorous compound include phosphoric acid, polyphosphoric acid, phosphonic acid, phosphinic acid and salts thereof. Examples of the organic phosphorous compound include phosphates, phosphites and salts thereof. Possible examples of the salt include metal salts such as sodium salts, potassium salts and barium salts (alkali metal salts, salts of alkaline earth metal hydroxides, etc.); ammonium salts; and salts of amines such as triethanolamine. These phosphorous compounds can be used solely as one species or in a combination of two or more species. The phosphorous compound is not chemically bonded to the base polymer in the PSA layer; it is separated from the base polymer or exits as being separable or movable with respect to the base polymer.

(Phosphate)

In some preferable embodiments, as the phosphorous compound, a phosphate is used. Examples of the phosphate include alkyl phosphates such as lauryl phosphate and a lauryl phosphate salt; and a phosphate having an oxyethylene chain and a salt thereof. The salt can be, for instance, sodium salts, potassium salts, barium salts and triethanolamine salts of these phosphates. In the following, unless otherwise noted, the “phosphate” includes a salt. In particular, it is more preferable to use a phosphate having an oxyethylene chain. Here, the oxyethylene chain refers to a structural moiety in chain form that includes at least one ethylene oxide (EO) unit and may further include other oxyalkylene Unit(s)(e.g. oxyalkylene unit(s) with about 3 to 6 carbon atoms). One favorable example of the oxyethylene chain-containing phosphate is a phosphate having an oxyethylene chain formed with an EO unit or repeats of this. For instance, a phosphate represented by the next general formula (a) or a salt thereof can be preferably used.

In the general formula (a), R¹ is —OH or —(OCH₂CH₂)_(n)OR³; R² represents —(OCH₂CH₂)_(m)OR⁴; n and m indicate the number of moles of EO added. The number of moles of EO added, n, is an integer between 1 and 30; it can be typically an integer between about 1 and 20, preferably an integer between about 1 and 10, for instance, an integer between about 1 and 8. The number of moles of EO added, n, is preferably an integer between about 1 and 6, or yet more preferably an integer between 1 and 4 (e.g. 2 and 4). In the general formula (a), the number of moles of ED added, m, can be typically about the same as the number of moles of EO added for n; n and m may be identical or different. R³ and R⁴ are mono-valent organic groups (typically hydrocarbon groups); for instance, each can be individually a group selected among an alkyl group, cycloalkyl group, aryl group, alkylaryl group, and arylalkyl group. R³ and R⁴ are preferably linear or branched alkyl groups, aryl groups or alkylaryl groups. R³ and R⁴ are individually an organic group with 1 to 30 carbon atoms, or possibly an organic group with 6 or more (preferably 8 or more, e.g., 11 or more) carbon atoms. In a preferable embodiment, R³ and R⁴ can be organic groups with 20 or fewer or preferably 18 or fewer, for instance, 15 or fewer carbon atoms. The phosphate salts represented by the general formula (a) can be, for instance, sodium salts, potassium salts barium salts and triethanolamine salts of these phosphates. For the phosphate, solely one species or a combination of two or more species can be used.

Examples of the phosphates include polyoxyethylene alkylphosphoric acid esters such as polyoxyethylene tridecyl ether phosphate, polyoxyethylene lauryl ether phosphate, and polyoxyethylene octadecyl ether phosphate; and polyoxyethylene alkyl aryl phosphoric acid esters such as polyoxyethylene nonyl phenyl ether phosphate, polyoxyethylene octyl phenyl ether phosphate, polyoxyethylene dinonyl phenyl ether phosphate, and polyoxyethylene dioctyl phenyl ether phosphate. In some embodiments, a phosphoric acid ester having a molecular weight of 150 to 5000 can be preferably used.

(Phosphite)

In other preferable embodiments, as the phosphorous compound, a phosphite is used. Examples of the phosphite include aliphatic phosphites, aromatic phosphites, aliphatic aromatic phosphites and salts thereof. An aliphatic aromatic phosphite has an aliphatic ester group and an aromatic ester group. In an embodiment where the phosphite is an alkyl phosphite, the alkyl group in the phosphite can be a linear, branched or alicyclic alkyl group. In an embodiment where the phosphite is an aryl phosphite, the aryl group in the phosphite can be an aryl group or an alkyl aryl group. The number of carbon atoms in the alkyl group is, for instance, 1 to 30, possibly 2 or higher (e.g. 4 or higher); and 20 or lower, preferably 18 or lower, for instance, possibly 15 or lower. The number of carbon atoms in the aryl group is 6 or higher (preferably 8 or higher, e.g. II or higher); and possibly 30 or lower (typically 20 or lower, preferably 10 or lower, e.g. 8 or lower). Examples of the salt include sodium salts, potassium salts, barium salts and triethanolamine salts of the phosphites. Hereinafter, unless otherwise noted, the “phosphite” includes a salt. The phosphites can be used solely as one species or in a combination of two or mom species.

As the phosphite, both a phosphorous acid diester having two ester groups and a phosphorous acid triester having three ester groups can be used. In particular, a phosphorous acid diester is preferable. Examples of the phosphorous acid diester include dialkyl phosphites, monoalkyl monoaryl phosphites and diaryl phosphites. Specific examples of the phosphorous acid diester (hydrogenphosphite) include alkyl hydrogenphosphites such as dimethyl hydrogenphosphite, diethyl hydrogenphosphite, diisopropyl hydrogenphosphite, dibutyl hydrogenphosphite, diisobutyl hydrogenphosphite and bis(2-ethylhexyl) hydrogenphosphite; and aryl hydrogenphosphites such as diphenyl hydrogenphosphite. Among them, diphenyl hydrogenphosphite is preferable.

The molecular weight of the phosphite is not particularly limited and is, for instance, 150 or higher, or possibly 200 or higher. The maximum molecular weight is not particularly limited and is, for instance, 10000 or lower. From the standpoint of the tendency to transfer to the Low-E layer surface, it is suitably 5000 or lower, possibly 3000 or lower, 1000 or lower, or even 500 or lower (e.g. 300 or lower).

The molecular weight of the phosphorous compound is not particularly limited and has at least the lowest possible molecular weight for phosphoric acid, phosphonic acid or phosphinic acid. It can be, for instance, 100 or higher, or even 150 or higher (e.g. 200 or higher). The maximum molecular weight is not particularly limited and is, for instance, 10000 or lower. From the standpoint of the tendency to transfer to the Low-E layer surface, it is suitably 5000 or lower, possibly 3000 or lower, 1000 or lower or even (e.g. 500 or lower).

The PSA layer can include the phosphorous compound in an amount suited for enabling film formation in the Low-E layer, not limited to a particular range. From the standpoint of prevention of Low-E layer alteration, the phosphorous compound content in the PSA layer is possibly about 0.01% by weight or higher, suitably about 0.05% by weight or higher, also possibly about 0.1% by weight or higher, about 0.5% by weight or higher, or even about 1% by weight or higher (e.g. about 2% by weight or higher). The phosphorous compound content in the PSA layer can be, for instance, about 30% by weight or lower. In view of the impact on the Low-contaminating properties of the adherend surface and the adhesive properties, it is possibly about 15% by weight or lower (e.g. about 10% by weight or lower), suitably about 5% by weight or lower, or possibly even about 3% by weight or lower (e.g. about 2% by weight or lower).

The phosphorous compound content can be considered the same as the amount added in this Description. Alternatively, the phosphorous compound content can be quantified based on an ICP (inductively coupled plasma) method. The specific quantification method is as follows: Approximately 10 mg of PSA of interest is collected in a Teflon® container. To this, a phosphorous compound is added. The container is sealed and then irradiated with microwaves to carry out pressurized acid digestion at a maximum temperature of 220° C. Upon complete digestion, ultrapure water is added to a constant volume of 20 mL. After suitable dilution, quantitative P analysis is performed by ICP-AES (ICP atomic emission spectroscopy). From the measured value, the phosphorous compound can be quantified. As the digestion device, product name MARS 5 available from CEM Corporation or a similar device can be used. As the KP-AES, product name SPS-3520UV available from Hitachi High-Tech Science Corporation or a similar system can be used. The quantification method for the phosphorous compound is not limited to the method described above. Various known quantification methods suited for the component to be quantified can be employed.

(Rust Inhibitor)

The PSA layer disclosed herein may include or may be fie of a rust inhibitor. The PSA layer according to some preferable embodiments may include a rust inhibitor. The rust inhibitor is not particularly limited. Examples include amine compounds, azole-based compounds, nitrites, ammonium benzoate, ammonium phthalate, ammonium stearate, ammonium palmitate, ammonium oleate, ammonium carbonate, dicyclohexylaminebenzoic acid salts, urea, urotropin, thiourea, phenyl carbamate, and cyclohexylammonium-N-cyclohexyl carbamate (CHC). These rust inhibitors can be used singly as one species or in a combination of two or more species. Among them, amine-based compounds and azole-based compounds are preferable.

The amount of rust inhibitor (e.g. an amine-based compound (amine-based rust inhibitor) or an azole-based compound (azole-based rust inhibitor) is not particularly limited. It can be, for instance, 0.01 part by weight or greater (typically 0.05 part by weight or greater) to 100 parts by weight of the base polymer. From the standpoint of obtaining greater anti-erosion effects, the amount may be 0.1 part by weight or greater, 0.3 part by weight or greater, or even 0.5 part by weight or greater. On the other hand, from the standpoint of the prevention of erosion due to components and the PSA's cohesive strength, the rust inhibitor content is suitably below 8 parts by weight to 100 parts by weight of the base polymer; or it is possibly 6 parts by weight or less, preferably 5 parts by weight or less, for instance, 3 parts by weight or less, or even 1 part by weight or less. The art disclosed herein can be preferably implemented in an embodiment using essentially no rust inhibitor.

(Other Components, Etc.)

The PSA composition can comprise, as necessary, a known tackifier such as a rosin-based tackifier, terpene-based tackifier and hydrocarbon-based tackifier. From the standpoint of avoiding an excessive increase in peel strength, the amount of tackifier is preferably about 5 parts by weight or less to 100 parts by weight of the base polymer, or more preferably about 1 part by weight or less. For the protective sheet disclosed herein, the adhesive strength can be effectively controlled by the base polymer's composition and Tg as well as PSA's gel fraction, etc.; and therefore, the protective sheet can be preferably made in an embodiment using no tackifier as well.

The PSA composition may comprise, as necessary, various optional additives generally known in the field of PSA compositions, such as viscosity-adjusting agent (viscosifiers, etc.), crosslinking accelerator, plasticizer, softener, filler, anti-static agent, anti-aging agent, UV-absorber, antioxidant, photo-stabilizing agent and defoamer. As the optional additive, an optional polymer different from the base polymer (e.g. an acrylic polymer) can be used as well. The optional polymer content is, for instance, about 10% by weight or less (e.g. about 1% by weight or less) of the PSA composition. The PSA composition disclosed herein may be essentially free of the optional polymer. In the PSA composition according to same embodiments, the amount of plasticizer such as aliphatic acid ester can be limited to, for instance, below 10 parts by weight (e.g. below 1 part by weight) to 100 parts by weight of base polymer. In typical, the PSA composition may be essentially free of a plasticizer. The art disclosed herein can be preferably implemented in an embodiment essentially free of an anti-static agent (possibly a conducting agent) such as an ionic compound (e.g. ionic liquid, alkaline metal salt). With respect to other matters about these various optional additives, various heretofore known additives and methods can be selected based on technical common knowledge. Because these additives do not characterize the present invention in particular, details are omitted.

In the art disclosed herein, in an embodiment using a water-dispersed PSA composition for PSA layer formation, the PSA composition can be prepared, for instance, by mixing an acrylic polymer dispersion in aqueous liquid obtained by emulsion polymerization using a surfactant with other components (e.g. crosslinking agent, etc.) used as necessary. For instance, it is possible to use a polymerization reaction mixture obtained by emulsion polymerization or the polymerization reaction mixture subjected as necessary to a treatment such as pH adjustment (e.g. neutralization), non-volatile content adjustment and viscosity adjustment.

While no particular limitations are imposed, from the standpoint of efficient drying, etc., the non-volatile content (NV) of the PSA composition can be about 20% by weight or higher (typically about 30% by weight or higher, preferably about 40% by weight or higher). From the standpoint of the ease of application, etc., it can be about 75% by weight or lower (typically about 70% by weight or lower, preferably about 60% by weight or lower).

(Formation of PSA Layer)

The PSA layer can be formed based on a known method ter forming PSA layers in PSA sheets. For instance, it is preferable to employ a direct method where the PSA composition is directly provided (typically applied) to the substrate and allowed to cure to form a PSA layer. Alternatively, it is also possible to employ a transfer method where the PSA composition is provided to a releasable surface (release face) and allowed to cure to form a PSA layer on the surface and the resulting PSA layer is transferred to the substrate. As the release face, the surface of a release liner, the substrate's backside treated with release agent, or the like can be used. While the PSA layer is typically formed in a continuous form, it can be formed in a regular or random pattern of dots, stripes, etc.

The PSA composition can be applied, using a heretofore known coater, for instance, a gravure roll coater, reverse roll coater, kiss roll coater, dip roll coater, die coater, bar coater, knife coater and spray coater. Alternatively, the PSA composition can be applied by immersion, curtain coating, etc. From the standpoint of accelerating the crosslinking reaction, increasing the productivity, etc., the PSA composition is preferably dried with heat. The drying temperature is possibly, for example, about 40° C. to 150° C. or preferably about 50° C. to 130° C. (e.g. 60° C. to 100° C.). Alter dried, the PSA composition can be allowed to further age for purposes such as adjusting the distribution or migration of components in the PSA layer, advancing the crosslinking reaction, and lessening the strain possibly present in the substrate and the PSA layer.

(Thickness of PSA Layer)

No particular limitations are imposed on the thickness of the PSA layer constituting the protective sheet disclosed herein. From the standpoint of preventing adhesive transfer to the adherend, the thickness of the PSA layer is usually about 50 μm or less, suitably about 30 μm or less, preferably about 15 μm or less, or more preferably about 8 μm or less (e.g. less than 6 μm). In other embodiments, from the standpoint of the case of removal, etc., the thickness of the PSA layer is suitably about 5 m or less, about 4 μm or less, or possibly, for instance, 3 μm or less. From the standpoint of the adhesion, the thickness of the PSA layer is suitably about 0.5 μm or greater, preferably about 1 μm or greater, or more preferably greater than 2 μm. The thickness of the PSA layer may be greater than 3 μm, for instance, greater than 4 μm.

<Substrate Layer>

The protective sheet disclosed herein may include a substrate layer. As the substrate layer, resin film, a rubber sheet, a foam sheet, a composite of these, etc., can be used. Examples of the rubber sheet include natural rubber sheets and butyl rubber sheets. Examples of the foam sheet include polyurethane foam sheets, and polychloroprene rubber foam sheets.

The art disclosed herein can be preferably applied to a protective sheet wherein the substrate layer is resin film. The concept of ‘resin film’ here refers to film typically obtained by molding a thin layer from a resin composition primarily comprising resin components as described below; it should be distinguished from so-called non-woven and woven fabrics. In other words, the concept of resin film excludes non-woven and woven fabrics. Preferable resin film is essentially not foamed. In other words, non-foamed resin film can be preferably used. Here, the non-foamed resin film refers to resin film that has not been deliberately subjected to a foaming process. In particular, the resin film may have an expansion ratio lower than about 1.1 (e.g. lower than 1.05, typically lower than 1.01).

Examples of the resin components forming the resin film include polyolefinic resins (polyethylene, polypropylene, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer, etc.), poly(vinyl chloride)-based resins (typically soft poly(vinyl chloride)-based resin); poly(vinyl acetate)-based resin, polyurethane-based resins (ether-based polyurethane, ester-based polyurethane, carbonate-based polyurethane, etc.), urethane (meth)acrylate-based resin, thermoplastic elastomers (olefinic elastomer, styrene-based elastomer, acrylic elastomer, etc.), polyester-based resins (polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polybutylene naphthalate, etc.), polycarbonate-based resin, polyamide-based resin, polyimide-based resin, fluororesin and cellulose-based resins such as cellophane resin. Among these resins, solely one species or a combination of two or more species can be used. Favorable examples of the resin film include polyolefinic resin film, polyester-based resin film and vinyl chloride-based resin film.

While no particular limitations are imposed, in the protective sheet according to some embodiments, it is preferable to use a substrate layer that comprises, as its primary component(s), one, two or more species of resin selected from the group consisting of polyolefinic resin, poly(vinyl chloride)-based resin, polyurethane-based resin, thermoplastic elastomer and polyester-based resin (typically a substrate layer comprising such resin in an amount exceeding 50% by weight). In other embodiments, in view of the performance, ease of handling, costs, etc., a substrate layer comprising a polyolefinic resin layer, polyester-based resin layer or polyvinyl chloride-based resin layer can be preferably used. Among the resin materials, in view of the heat stability, the lightness of weight, etc., polyolefinic resins, polyurethane-based resins and olefinic elastomers are preferable; in view of the handling properties, etc., polyolefinic resins and olefinic elastomers are particularly preferable.

The protective sheet disclosed herein can be preferably made in an embodiment comprising a substrate layer that comprises a polyolefinic resin as the primary component (e.g. more than 50% by weight), that is, an embodiment wherein the substrate layer is polyolefinic resin film. For instance, it is preferable to use polyolefinic resin film in which 50% by weight or more of the entire substrate layer is polyethylene (PE) resin or polypropylene (PP) resin. In other words, in the polyolefinic resin film, the combined amount of PE resin and PP resin may account for 50% by weight or more of the entire substrate layer. The polyolefinic resin film can be a blend of PE and PP resins.

The PP resin may comprise, as the primary component, various polymer species (propylene-based polymers) that comprise propylene as a monomer unit. The PP resin may be essentially formed of one, two or more species of propylene-based polymer. The concept of propylene-based polymer here includes homopolypropylene as well as a random copolymer of propylene and other monomer(s) (random polypropylene) and a block copolymer (block polypropylene). The concept of propylene-based polymer hem includes, for instance, the following species:

Propylene homopolymer (homopolypropylene), for instance, isotactic polypropylene;

Random copolymer (random polypropylene) of propylene and other α-olefin(s)(typically, one, two or more species selected from ethylene and α-olefins having 4 to 10 carbon atoms), preferably random polypropylene comprising propylene as the primary monomer (i.e. the monomer accounting for 50% by weight or more of the total monomer content);

Block copolymer (block polypropylene) of propylene and other α-olefin(s)(typically one, two or more species selected from ethylene and α-olefins having 4 to 10 carbon atoms), preferably block polypropylene comprising propylene as the primary monomer (i.e. the monomer accounting for 50% by weight or more of the total monomer content).

The PE resin may comprise, as the primary component, various types of polymer (ethylene-based polymer) comprising ethylene as a monomer. The PE resin may be essentially formed of one, two or more species of ethylene-based polymer. The ethylene-based polymer can be an ethylene homopolymer or a copolymer (random copolymer, block copolymer, etc.) of ethylene as the primary monomer and other α-olefin(s) as secondary monomer(s). Favorable examples of the α-olefins include α-olefins having 3 to 10 carbon atoms such as propylene, 1-butene (which can be a branched 1-butene), 1-hexene, 4-methyl-1-pentene and 1-octene. For instance, it is preferable to use PE resin that comprises, as the primary component, an ethylene-based polymer in which an α-olefin as the secondary monomer is copolymerized up to about 10% by weight (typically up to about 5% by weight).

The PE resin may comprise a copolymer of ethylene and a monomer (functional monomer) containing other functional group(s) in addition to a polymerizable functional group, copolymer of an ethylene-based polymer copolymerized with such a functional monomer, or the like. Examples of a copolymer of ethylene and a functional monomer include ethylene-vinyl acetate copolymers (EVA), ethylene-acrylic acid copolymers (EAA), ethylene-methacrylic acid copolymers (EMAA), ethylene-methyl acrylate copolymers (EMA), ethylene-ethyl acrylate copolymers (EEA), ethylene-methyl methacrylate copolymers (EMMA), and copolymers of ethylene and (meth)acrylic acid (i.e. acrylic acid and/or methacrylic acid) crosslinked by metal ions.

The PE resin is not particularly limited in density. The concept of PE resin here includes all of the following: high density polyethylene (HDPE), medium density polyethylene (MDPE), low density polyethylene (LDPE) and linear low density polyethylene (LLPDE). In an embodiment, the density of the PE resin can be, for instance, about 0.90 g/cm³ to 0.94 g/cm³. Preferable PE resins include LDPE and LLDPE. The PE resin may comprise one, two or more species of LDPE and one, two or more species of LLDPE. There are no particular limitations to the respective blend ratios of LDPE and LLDPE, or to the LDPE to LLDPE blend ratio. They can be suitably selected to form a PE resin having desirable properties. As the substrate layer of the protective sheet disclosed herein, it is preferable to use polyethylenic resin film such as LLDPE film whose LLDPE content is higher than 50% by weight (preferably about 75% by weight or higher, e.g. about 90% by weight or higher) and LDPE film whose LDPE content is higher than 50% by weight (preferably about 75% by weight or higher, e.g. about 90% by weight or higher). Laminate resin film comprising such polyethylenic resin film as a component can be used as well.

The resin film (e.g. polyolefinic resin film) used as the substrate layer of the protective sheet disclosed herein may comprise, as necessary, suitable components allowable in the substrate layer. Examples of additives that can be suitably added include filler, colorant (pigment such as inorganic pigment, dye), antioxidant, photostabilizer (including radical scavenger and UV absorber), antistatic agent, plasticizer, slip agent, and anti-blocking agent. Each additive can be added, for instance, in an amount similar to a typical amount in the field of resin film used as substrate layers and the like of protective sheets.

The substrate layer may have a mono-layer structure or a multi-layer structure formed of two, three or more layers. In a multi-layer structure, it is preferable that at least one layer (preferably each layer) is formed of aforementioned resin film. For instance, in a preferable substrate layer, 75% or more (more preferably 90% or more) of the thickness is attributed to mono-layer or multi-layer (typically mono-layer) polyolefinic resin film. The substrate layer may be entirely formed of mono-layer or multi-layer polyolefinic resin film. From the standpoint of the cost-effectiveness, it is preferable to use a substrate layer formed of mono-layer resin film (e.g. LLDPE film, LDPE film, etc.).

The method for producing the substrate layer can be suitably selected among heretofore known methods and is not particularly limited. For instance, when resin film is used as the substrate layer, it is possible to use resin film fabricated by suitably employing a heretofore known general film-forming method such as inflation molding, extrusion, T-die cast molding, and calendar roll molding.

In an embodiment where at least one face (the PSA layer-side face) of the substrate layer is a resin film surface, the resin film surface can be subjected to a heretofore known surface treatment such as corona discharge treatment, plasma treatment, ozone exposure, flame exposure, UV irradiation, acid treatment, alkali treatment, and primer coating. These surface treatments may enhance the tightness of adhesion between the substrate layer and the PSA layer, or the anchoring of the PSA layer onto the substrate layer. In an embodiment using polyolefinic resin film as the substrate layer, it is particularly meaningful to provide these surface treatments.

The thickness of the substrate layer constituting the protective sheet disclosed herein is not particularly limited. The thickness of the substrate layer can be, for instance, about 800 μm or less (typically about 250 μm or less). In some embodiments, the thickness of the substrate layer (typically, non-foamed resin film) is preferably about 150 μm or less, more preferably about 100 μm or less, or yet more preferably less than 65 μm, for instance, less than 55 μm. With decreasing thickness of the substrate layer, the protective sheet tends to exhibit greater conformability to the adherend shape while its lifting and peeling tend to be inhibited. From the standpoint of adherend protection and handling properties, etc., the thickness of the substrate layer can be typically about 10 μm or greater, preferably about 25 μm or greater, more preferably grater than about 30 μm, or yet more preferably greater than 40 μm, or possibly, for instance, greater than 45 μm.

<Properties of Protective Sheet>

(Initial to-Glass Adhesive Strength)

The protective sheet disclosed herein suitably has an initial peel strength (initial to-glass peel strength) of about 0.01 N/20 mm or greater, determined at a tensile speed of 0.3 m/min at 180° peel angle after applied to a Low-E glass plate for 30 minutes. In some embodiments, the initial peel strength can be about 0.05 N/20 mm or greater (e.g. about 0.1 N/20 mm or greater). In some preferable embodiments, the initial peel strength can be about 0.5 N/20 mm or greater (e.g. about 1 N/20 mm or greater), or even about 1.5 N/20 mm or greater. The protective sheet showing such initial peel strength can adhere well to an adherend in relatively short time with less likelihood to lift off the adherend and provide good protection. The maximum initial peel strength is not particularly limited. From the standpoint of the light peel, it is suitably about 5 N/20 mm or less, or preferably about 2.5 N/20 mm or less (e.g. about 2 N/20 mm or less). The initial peel strength is determined by the method described below.

[Initial Peel Strength]

The protective sheet to be measured is cut to a 20 mm wide by 100 mm long strip to prepare a test piece. In a standard environment at 23 C, 50% RH, with a 2 kg rubber roller moved back and forth twice, the test piece is press-bonded to a Low-E glass plate as the adherend. The sample is stored in the standard environment for 30 minutes. In the same standard environment, using a universal tensile tester, the initial peel strength (initial to-glass adhesive strength)(N/20 mm) is determined at a tensile speed of 0.3 m/min, at 180° peel angle. As the Low-E glass plate, product number RSFL6AS (100 mm×100 mm) available from Nippon Sheet Glass Co., Ltd. is used. It is noted that as the adherend, any Low-E glass plate can be used without particular limitations and a product comparable to RSFL6AS or other commercial Low-E glass plate can be used as well.

(Aged to-Glass Adhesive Strength)

The protective sheet disclosed herein preferably has an aged peel strength (aged to-glass adhesive strength) of about 5 N/20 mm or less, determined at a tensile speed of 0.3 m/min, at 180° peel angle, after applied to a Low-E glass plate and stored at 50° C. for 7 days. With the protective sheet satisfying this property, even when it is applied to the adherend for a relatively long time, the aged adhesive strength is sufficiently suppressed and its light peel from adherend can be maintained. Thus, it shows excellent efficiency of removal from adherends. With the protective sheet wherein the aged peel strength is about 4 N/20 mm or less (more preferably about 2 N/20 mm or less), greater efficiency of removal can be obtained. From the standpoint of inhibiting lifting and peeling while the adherend is protected (e.g. during processing of the adherend with the protective sheet applied thereon), the aged peel strength is suitably about 0.05 N/20 mm or greater, preferably about 0.1 N/20 mm or greater, or more preferably about 0.3 N/20 nm or greater. The aged peel strength can also be about 1 N/20 mm or greater. The aged peel strength is determined by the method described below.

[Aged Peel Strength]

The protective sheet to be measured is cut to a 20 mm wide by 100 mm long strip to prepare a test piece. In a standard environment at 23° C., 50% RH, with a 2 kg rubber roller moved back and forth twice, the test piece is press-bonded to a Low-E glass plate as the adherend. The sample is stored in an environment at 50° C. for seven days and then in a standard environment at 23° C., 50% RH for one hour. Subsequently, in the same standard environment, using a universal tensile tester, the aged peel strength (aged to-glass adhesive strength)(N/20 mm) is determined at a tensile speed of 0.3 m/min, at 180° peel angle. The Low-E glass plate used as the adherend is the same as the one used in the initial peel strength measurement.

(Peel Strength Ratio)

While no particular limitations are imposed, the protective sheet disclosed herein may have a ratio of aged peel strength P₂ (N/20 mm) to initial peel strength P₁ (N/20 mm) (i.e. a P₂/P₁ ratio value) of 5 or lower. A small P₂/P₁ ratio value indicates a small increase in peel strength with aging. By this, initial adhesion and light peel during removal are favorably combined. From such a standpoint, the P₂/P₁ ratio is preferably 4 or lower, more preferably 3 or lower, or yet more preferably 2 or lower, for instance, 1.8 or lower, 1.5 or lower, or even 1.3 or lower. The P₂/P₁ ratio is typically 0.8 or higher; it can be, for instance, 1 or higher.

(VOC Emission)

From the standpoint of environmental sanity, the protective sheet disclosed herein preferably can have a total amount of volatile organic compounds (VOC) of 1000 μg or less emitted from 1 g thereof (possibly including a substrate layer and a PSA layer, but not a release liner) when heated at 80° C. for 30 minutes (or, for short, a VOC emission of 1000 μg/g or less). The VOC emission is preferably 500 μg/g or less (e.g. 300 μg/g or less, typically 100 μg/g or less). The VOC emission is determined by the next method.

[VOC Test]

The protective sheet is cut to a prescribed size (to an about 5 cm² sized area, here) and the release liner is removed to prepare a test piece. The test piece is placed and sealed in a 20 mL vial. The vial is then heated at 80° C. for 30 minutes and 1.0 mL of the heated gas (sample gas) is injected into a gas chromatograph (GC), using a head space autosampler (IISS). Based on the resulting gas chromatogram, the amount of gas emitted from the test piece is determined as an n-decane equivalent amount. From the resulting value, the VOC emission is determined per gram of protective sheet (μg/g, excluding the release liner). The n-decane equivalent amount is determined by applying a calibration curve prepared in advance for n-decane, with the intensities of emission gas obtained by GC Mass seen as equivalent to the intensities of n-decane. The HSS and GC settings are as follows:

HSS: model 7694 available from Agilent Technologies

Heating time: 30 min

Pressurization time: 0.12 min

Loop filling time: 0.12 min

Loop equilibration time: 0.05 min

Injection time: 3 min

Sample loop temperature: 160° C.

Transfer line temperature: 200° C.

GC: model 6890 available from Agilent Technologies

Column: J&W capillary column, product name DB-fMAP, available from GL Science (0.533 mm inner diameter×30 m length, 1.0 μm thick membrane)

Column temperature: 250° C. (temperature raised at 10° C./min from 40° C. to 90° C., followed at 20° C./min to 250° C. and maintained there for 5 min)

Colum pressure: 24.3 kPa (constant flow mode)

Carrier gas: helium (5.0 mL/min)

Injection port: split (split ratio 12:1)

Injection port temperature: 250° C.

Detector: FID

Detector temperature: 250° C.

The protective sheet disclosed herein may have a level of alteration resistance graded as no discoloration in the Low-E glass plate discoloration test (at 40° C. and 92% RH for 2 weeks) carried out by the method described later in Examples. The protective sheet satisfying this property can show excellent alteration resistance in applications for protecting Low-E glass plates.

<Applications>

The protective sheet disclosed herein is favorable as a protective sheet for a glass plate used as a building material such as window glass, etc. The glass plate subject to application can be a Low-E glass plate having a Low-E layer on one face. The Low-E layer disclosed herein comprises a tin component. Other than this, it is not particularly limited. According to the art disclosed herein. Low-E layer alteration is prevented or inhibited in an embodiment where the entry of a component capable of causing Low-E layer alteration is blocked with the film formed of the product of reaction between the tin component of the Low-E layer and a specific phosphorous compound in the PSA layer and. A general Low-E layer includes a metal layer, an oxide layer such a metal oxide layer and a nitride layer such as a silicon nitride layer; and can be typically formed by a known or conventional method such as sputtering. Examples of the material forming each layer in the Low-E layer include TiO₂, ZrO₂, Si_(X)N_(Y), ZnO_(X), Ag, NiCrO_(X), SnO₂ and ZTO (oxide of zinc and tin). As the infrared-reflective layer, a Ag layer is preferably used. The Ag layer can be formed of Ag alone or an alloy of Ag and other metal (Pd, etc.). The Low-E layer may typically have one, two or more tin-containing layers. While no particular limitations are imposed, in the Low-E layer according to some embodiments, the Ag layer can be present between any two of oxide layers such as TiO₂ layers, ZrO₂ layers, ZnO_(X) layers, NiCrO_(X) layers, SnO₂ layers and ZTO layers or nitride layers such as Si_(X)N_(Y) layers. The material of the Low-E layer's outermost surface (to which the protective sheet is applied) is often an oxide such as TiO₂, ZrO₂, ZnO_(X), NiCrO_(X), SnO₂ and ZTO or a nitride such as Si_(X)N_(Y); it typically is not a metal such as Ag. Depending on the purpose and required properties, the Low-E layer may have a multi-layer structure with 5 or more layers, for instance, 10 or more layers, or even 15 or more layers. The thickness of each layer is not particularly limited. It is usually 1000 Å or less, or suitably about 10 Å to 700 Å, for instance, about 30 Å to 300 Å. The thickness (overall thickness) of the Low-E layer can be about 10 nm to 1000 nm (e.g. about 50 nm to 500 μm).

In an embodiment where the Low-E layer of the Low-E glass plate has a tin-containing layer, one tin-containing layer has a thickness of, for instance, about 100 μm or less, or suitably about 70 nm or less (e.g. about 50 nm or less, or even about 30 nm or less); and, for instance, about 1 nm or greater, or suitably about 3 μm or greater (e.g. about 8 μm or greater). Typical examples of the tin-containing layer include a tin oxide-containing layer. The tin oxide-containing layer can be formed from tin oxide or an oxide of tin and other element (e.g. zinc).

The tin-containing layer can be present on the outer surface (outermost surface) of the Low-E layer or internal to the Low-E layer. In an embodiment where the tin-containing layer is internal to the Low-E layer, the distance (thickness) from the Low-E layer's outer surface to the tin-containing layer is not particularly limited and it is, for instance, about 300 nm or less, or suitably about 200 nm or les (e.g. about 100 nm or less). In such an embodiment, the effect of the art disclosed herein can be preferably obtained. The minimum distance (thickness) from the Low-E layer's outer surface to the tin-containing layer is not particularly limited and it is, for instance, about 1 nm or greater, or possibly about 10 nm or greater.

In producing the glass plate, the Low-E layer surface may be left exposed until two glass plates including the Low-E glass plate are assembled into a pair-glass (e.g. dual-pane glass) with the Low-E-layer-side surface on the inside. The protective sheet disclosed herein is preferably used to prevent the Low-E layer surface from damage, wear, degradation, corrosion, etc. In other words, the protective sheet can be used as a protective sheet for a Low-E layer surface. In the protection period, the Low-E glass plate having the protective sheet applied thereon may be in a laminate form where the Low-E glass plate and the protective sheet are layered. Accordingly, the art disclosed herein provides a laminate having a Low-E glass plate and a protective sheet. The particulars of the Low-E glass plate and protective sheet are as described above and thus are not repeated here.

In the laminate, the protective sheet is preferably adhered to the Low-E glass plate with a 180° peel strength of 5 N/20 mm or less. From the standpoint of the light peel, the peel strength is more preferably about 2.5 N/20 mm or less (e.g. about 2 N/20 mm or les). The peel strength is, fir instance, about 0.01 N/20 mm or greater, or suitably about 0.05 N/20 mm or greater (e.g. about 0.1 N/20 mm or greater). From the standpoint of the tightness of adhesion between the Low-E glass plate and the protective sheet, it is preferably about 0.5 N/20 mm or greater (e.g. about 1 N/20 mm or greater), or possibly even 1.5 N/20 mm or greater. The protective sheet laminated to the Low-E glass plate with such peel strength is less likely to sort of lift or peel from the Low-E glass plate and can provide good protection. For the peel strength measurement conditions, other than using the protective sheet applied to the Low-E glass plate, basically the same peeling conditions for the aforementioned initial peel strength measurement am applied. The peel strength (N/20 mm) is obtained by multiplying 20 mm and the quotient of the measured value (N) divided by the measured width (mm).

From the standpoint of the efficiency of removal, the protective sheet disclosed herein is preferably used on an adherend having a large surface area on which the peel strength tends to be limited. The protective sheet disclosed herein is preferably used in an embodiment where it covers the entire surface of an adherend having a width of about 1 m or greater, for instance, about 1.5 m or greater, or even 2 in or greater (typically about 3 in or greater or even about 3.3 m or greater). The length of the adherend surface is equal to or greater than the width. In a preferable embodiment, it is preferably used in an embodiment where it entirely covers the surface of one face of a large flat plate (favorably, a flat plate with a smooth surface). In particular, glass plates used for building materials such as window glass are becoming progressively larger in view of efficient production, transportation, etc. It is preferably used in an embodiment where it covers the entire surface of a glass plate (typically the entire Low-E layer surface of the Low-E glass plate) having a large surface area (e.g. with a surface width of greater than 2.6 m, typically about 3 m or greater, or even about 3.3 m or greater). A preferable embodiment of the art disclosed herein can bring about great alteration resistance while maintaining light peel with respect to an adherend having such a large surface area.

The protective sheet disclosed herein may further show suppressed aged adhesive strength and thus may provide good efficiency of removal even when, for instance, the period of adhesion to the adherend (which can be the protection period for the adherend) becomes relatively long (typically two weeks or longer, e.g. four weeks or longer). Thus, for instance, it can be favorably used in an embodiment where the protective sheet is removed &om the adherend (in particular, a Low-E glass plate) after being applied thereon for two weeks or more (e.g. four weeks or more).

Low-E glass plates have higher levels of heat blocking or thermal insulation as compared to conventional glass plates and can improve the efficiency to cool down or heat up indoor spaces; and therefore, they are widely used as building materials such as window glass. When used in manufacturing such materials, the art disclosed herein may indirectly contribute to energy saving and reduction of greenhouse gas emissions.

The matters disclosed by this description include the following:

(1) A method for producing a glass unit, the method comprising:

a step (A) of obtaining a Low-E glass plate having a Low-E layer;

a step (B) of applying a protective sheet to a surface of the Low-E layer of the Low-E glass plate:

an optional step (C) of subjecting the Low-E glass plate to at least one process selected from the group consisting of transportation, storage, processing, washing and handling;

a step (D) of removing the protective sheet from the Low-E glass plate; and

a step (E) of assembling a glass unit using the Low-E glass plate:

wherein

the protective sheet has a PSA layer,

the Low-E layer comprises a tin component, and

the PSA layer includes a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group.

(2) The method according to (1) above, wherein the Low-E glass plate has a width of 1 m or greater. (3) The method according to (1) above, wherein the Low-E glass plate has a width of 2 m or greater. (4) The method according to (1) above, wherein the Low-E glass plate has a width greater than 2.6 m. (5) The method according to (1) above, wherein the Low-E glass plate has a width of 3 m or greater. (6) The method according to any of (1) to (5) above, wherein the Low-E layer comprises a tin-containing layer. (7) The method according to any of (1) to (5) above, wherein the Low-E layer comprises a tin oxide layer. (8) The method according to any of (1) to (7) above, wherein the Low-E layer has a thickness of 100 nm or less. (9) The method according to any of (1) to (8) above, wherein the step (B) includes a step of entirely covering one face of the Low-E glass plate with at least one said protective sheet. (10) The method according to any of (1) to (9) above, wherein the step (C) is essential and in the step (C), the Low-E glass plate is washed using water. (11) A method for protecting a Low-E glass plate, the method comprising a step (application step) of applying a protective sheet to a surface of a Low-E glass plate that has a Low-E layer, wherein

the protective sheet has a PSA layer,

the Low-E layer comprises a tin component, and

the PSA layer includes a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group.

(12) The method according to (11) above, wherein after the protective sheet is applied to the Low-E glass plate, a film is newly formed on/in the Low-E layer and the film comprises P and Sn as its constituent elements. (13) The method according to (12) above, wherein the film exists on an outer surface of the Low-E layer. (14) The method according to (12) above, wherein the film exists internal to the Low-E layer. (15) The method according to any of (12) to (14) above, wherein the film is formed within 24 hours after the protective sheet is applied to the surface of the Low-E glass plate. (16) The method according to any of (12) to (15) above, wherein the film has a thickness of 1 nm or greater and 20 nm or less. (17) The method according to any of (11) to (16) above,

the method further comprising a step (removal step) of removing the protective sheet from the Low-E glass plate, and

the method optionally including, between the application step and the removal step, at least one process selected from the group consisting of transportation, storage, processing, washing and handling of the Low-E glass plate with the protective sheet adhered thereon.

(18) The method according to (11) or (17) above, wherein

the Low-E glass plate has a width of 1 m or greater, and

the application step comprises a step of entirely covering one face of the Low-E glass plate with at least one of the protective sheet.

(19) The method according to any of (1) to (18) above, wherein the phosphorous compound is selected between a phosphate and a phosphite. (20) The method according to any of (1) to (19) above, wherein the Low-E layer comprises a tin-containing layer (e.g. a tin oxide-containing layer). (21) A protective sheet having a PSA layer, wherein

the PSA layer includes a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group.

(22) The protective sheet according to (21) above, wherein the phosphorous compound is selected between a phosphate and a phosphite. (23) The protective sheet according to (21) or (22) above, wherein the PSA layer is formed from a water-dispersed PSA composition. (24) The protective sheet according to any of (21) to (23) above, wherein the PSA layer is an acrylic PSA layer comprising an acrylic polymer, or a rubber-based PSA layer comprising a rubber-based polymer. (25) The protective sheet according to any of (21) to (24), having a substrate layer. (26) The protective sheet according to (25) above, wherein the substrate layer is formed from a resin film. (27) The protective sheet according to (21) to (26) above, having a 180° peel strength of 5 N/20 nm or less to Low-E glass plate. (28) The protective sheet according to any of (21) to (27), wherein the protective sheet is a Low-E glass plate protective sheet. (29) The protective sheet according to any of (21) to (27) above, wherein the protective sheet is used for protecting a Low-E glass plate having a Low-E layer comprising a tin component. (30) The protective sheet according to any of (21) to (27) above, wherein the protective sheet is used for protecting a Low-E glass plate that comprises a Low-E layer having a tin-containing layer. (31) The protective sheet according to any of (21) to (27) above, wherein the protective sheet is used for protecting a Low-E glass plate that comprises a Low-E layer having a tin oxide layer. (32) A laminate having a Low-E glass plate and a protective sheet protecting the Low-E glass plate surface, wherein

the Low-E glass plate has a Low-E layer comprising a zinc component,

the protective sheet has a PSA layer, and

the PSA layer includes a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group.

(33) The laminate according to (32) above, wherein a film is formed on/in the Low-E layer and the film comprises P and Sn as its constituent elements. (34) The laminate according to (33) above, wherein the film exists on an outer surface of the Low-E layer. (35) The laminate according to (33) above, wherein the film exists internal to the Low-E layer. (36) The laminate according to any of (33) to (35) above, wherein the film has a thickness of 1 nm or greater and 20 nm or less. (37) The laminate according to any of (33) to (36) above, wherein the phosphorous compound is selected between a phosphate and a phosphite. (38) The laminate according to any of (32) to (37) above, wherein the PSA layer is formed from a water-dispersed PSA composition. (39) The laminate according to any of (32) to (38) above, wherein the Low-E layer comprises a tin-containing layer. (40) The laminate according to an of (32) to (39) above, wherein the Low-E layer comprises a tin oxide layer. (41) The laminate according to any of (32) to (40) above, wherein the PSA layer is an acrylic PSA layer comprising an acrylic polymer or a rubber-based PSA layer comprising a rubber-based polymer. (42) The laminate according to any of (32) to (41) above, having a substrate layer. (43) The laminate according to (42) above, wherein the substrate layer is formed from a resin film. (44) The laminate according to any of (32) to (43) above, wherein the protective sheet is adhered to the Low-E glass plate with a 180° peel strength of 5n/20 mm or less. (45) A method for preventing or inhibiting alteration to a Low-E glass plate having a Low-E layer, the method comprising a step of providing a P—OR-group-containing phosphorous compound to the Low-E layer, wherein R in the P—OR group is a hydrogen atom or an organic group and the Low-E layer comprises a tin component. (46) The method according to (45) above, wherein after the protective sheet is applied to the Low-E layer, a film is newly formed on/in the Low-E layer and the film comprises P and Sn as its constituent elements. (47) The method according to (45) or (46) above, wherein with a protective sheet having a PSA layer comprising the phosphorous compound, the phosphorous compound is provided by applying the PSA layer to the Low-E layer. (48) The method according to (46) or (47) above, wherein the film exists on an outer surface of the Low-E layer. (49) The method according to (46) or (47) above, wherein the film exists internal to the Low-E layer. (50) The method according to any of (46) to (49) above, wherein the film has a thickness of 1 nm or greater and 20 nm or less. (51) The method according to any of (45) to (50) above, wherein the phosphorous compound is selected between a phosphate and a phosphite. (52) The method according to any of (45) to (51) above, wherein the Low-E layer includes a tin-containing layer. (53) The method according to (52) above, wherein the tin-containing layer is a tin oxide-containing layer. (54) A Low-E glass plate having a Low-E layer, wherein

the Low-E layer includes a film comprising P and Sn as its constituent elements.

(55) The Low-E glass plate according to (54) above, wherein the film exists on an outer surface of the Low-E layer. (56) The Low-E glass plate according to (54) above, wherein the film exists internal to the Low-E layer. (57) The Low-E glass plate according to any of (54) to (56) above, wherein the film has a thickness of 1 nm or greater and 20 nm or less. (58) The Low-E glass plate according to any of (54) to (57) above, wherein the Low-E layer includes a tin-containing layer which is different from the film. (59) The Low-E glass plate according to (58) above, wherein the tin-containing layer is a tin oxide-containing layer.

EXAMPLES

Several experimental examples related to the present invention are described below, but the present invention should not be limited to these experimental examples. In the description below, “part(s)” and “%” are by weight unless otherwise specified.

<Test Methods> [Discoloration Test of Low-E Glass Plate]

The protective sheet is cut to a 20 mm wide, 100 mm long strip to prepare a test piece. In a standard environment at 23° C. and 50% RH, the test piece is press-bonded to the Low-E layer surface of a test Low-E glass plate as the adherend with a 2 kg rubber roller moved back and forth twice. The sample is stored in an environment at 40° C. and 92% RH for two weeks and the protective sheet is then removed. With respect to the area protected with the protective sheet, the state of the glass plate surface is inspected under an optical microscope. The following grades are assigned; “Good” when no discoloration is observed and “Fail” when discoloration is observed.

<Preparation of Low-E Glass Plates for Testing> Preparation Example A1

Using a sputtering machine, on one face of a 3 mm thick float glass plate (available from Matsunami Glass Ind., Ltd.; 91% visible light transmission), the followings were formed in order by direct magnetron sputtering: a 10 nm thick titanium oxide layer (or sometimes abbreviated to as “TiO₂ layer” for convenience, hereinafter), a 10 nm thick tin oxide layer (or sometimes abbreviated to as “SnO₂ layer” hereinafter), a 15 nm thick Ag—Pd alloy layer (or sometimes abbreviated to as “Ag layer” hereinafter), a 10 nm thick tin oxide layer (SnO₂ layer) and a 10 nm thick titanium oxide layer (TiO₂ layer). Sintered titanium oxide was used as a target to form the titanium oxide layers and sputtering was carried out at a power density of 2.67 W/cm² at a process pressure of 0.4 Pa. During this, the amount of gas introduced to the sputtering chamber was adjusted to obtain an Ar to O₂ ratio of 98:2 (by volume). For the formation of the tin oxide layer, sintered tin oxide was used as the target and sputtering was carried out at a power density of 2.67 W/cm² at a process pressure of 0.4 Pa. During this, the amount of gas introduced into the sputtering chamber was adjusted so as to obtain an Ar to O₂ ratio of 98:2 (by volume). For the formation of the Ag—Pd alloy layer, using a metal target comprising silver and palladium at a weight ratio (Ag:Pd) of 96.4:3.6, sputtering was carried out at a power density of 1.33 W/cm² at a process pressure of 0.4 Pa. In this manner, was prepared a test Low-E glass plate A1 having TiO₂ layer, SnO₂ layer, Ag layer, SnO₂ layer and TiO₂ layer (outermost layer) laminated in this order.

Preparation Example A2

Low-E layers were laminated in the following order starting from the glass plate side: SnO₂ layer, Ag layer. SnO₂ layer (outermost layer). Otherwise, basically in the same manner as Preparation Example A1, was prepared a test Low-E glass plate A2.

Preparation of Protective Sheets> Preparation Example B1

Were mixed a starting monomer mixture comprising 58 parts of 2-ethylhexylacrylate, 40 parts of n-butyl methacrylate and 2 parts of acrylic acid with 3 parts of surfactant (trade name AQUALON KH-1025 available from Dai-ichi Kogyo Seiyaku Co., Ltd.: ammonium polyoxyethylene-1-(allyloxymethyl) alkyl ether sulfate with up to 30 moles of added EO) and 150 parts of deionized water. The resulting mixture was emulsified under nitrogen flow with an emulsifying machine (homo mixer) to prepare an emulsion of the starting monomers.

Into a reaction vessel equipped with a thermometer, nitrogen inlet, condenser and stirrer, was placed the emulsion and heated under nitrogen flow to a liquid temperature of 50° C. while stirring. To this, was added 0.03 part of 2,2′-azobis(2-methylpropionamidine)dihydrochloride (product name V-50 available from FUJIFILM Wako Pure Chemical industries, Ltd.) as polymerization initiator and the polymerization reaction was carried out for 5 hours while maintaining the liquid temperature around 50° C. To the resulting polymerization reaction mixture, was added ammonia water and adjusted. An aqueous dispersion of acrylic polymer was thus prepared.

To the aqueous dispersion, per 100 parts of non-volatiles therein, were mixed 2 parts of oxazoline-based crosslinking agent (product name EPOCROS WS-500 available from Nippon Shokubai Co., Ltd.) and 0.1 part of Phosphate A (trade name Phosphanol RP-710 available from Toho Chemical Industry Co., Ltd.; polyoxyethylene phenyl ether phosphate) to prepare a PSA composition according to this Example.

Of 55 μm thick polyethylene film having one face treated with corona discharge, onto the corona-treated face (first face), was applied the PSA composition with a bar coater to a dried thickness of 6 μm, was dried at 70° C. for two minutes and then aged at 50° C. for one day to prepare an adhesively single-faced PSA sheet having an acrylic PSA layer on one face of a substrate layer formed of the polyethylene film. The resulting PSA sheet was used as the protective sheet B1 according to this Example.

Preparation Examples B2-B4

Phosphate A was added to the PSA composition in the amounts shown in Table 1. Otherwise in the same manner as Preparation Example B1, were obtained Protective Sheets B2 to B4.

Preparation Example B5

In place of Phosphate A, was used 2.0 parts of Phosphate B (trade name Phosphanol GF-185 available from Toho Chemical industry Co., Ltd.; C₁₃H₂₇ alkyl phosphate) to 100 parts of acrylic polymer (non-volatiles of the aqueous acrylic polymer dispersion) to prepare a PSA composition. Otherwise in the same manner as Preparation Example B3, was obtained Protective Sheet B5.

Preparation Example 86

In place of Phosphate A, was used 2.0 parts of Phosphate C (trade name Phosphanol ED-200 available from Toho Chemical Industry Co., Ltd.; polyoxyethylene alkyl ether phosphate) to 100 parts of acrylic polymer (non-volatiles of the aqueous acrylic polymer dispersion) to prepare a PSA composition. Otherwise in the same manner as Preparation Example B3, was obtained Protective Sheet B6.

Preparation Example B7

In place of Phosphate A, was used 2.0 parts of a phosphite (diphenyl hydrogen phosphite available from Tokyo Chemical Industry Co., Ltd.) to 100 parts of acrylic polymer (non-volatiles of the aqueous acrylic polymer dispersion) to prepare a PSA composition. Otherwise in the same manner as Preparation Example 13, was obtained Protective Sheet B7.

Preparation Example B8

Phosphate A was not used. Otherwise in the same manner as Preparation Example B1, was obtained Protective Sheet B8.

Preparation Example B9

In place of Phosphate A, was used 2.0 parts of a P—OR-group-free phosphorous compound (trade name Omnirad 819 available from IGM Resins B.V.; bis(2,4,6-trimethylbenzoyl) phenylphosphine oxide) to 100 parts of acrylic polymer (non-volatiles of the aqueous acrylic polymer dispersion) to prepare a PSA composition. Otherwise in the same manner as Preparation Example B3, was obtained Protective Sheet B9.

Preparation Example B10

Into a four-neck flask equipped with a stirring blade, thermometer, nitrogen inlet and condenser, were placed 100 parts of butyl acrylate, 5 parts of acrylic acid and 0.2 part of benzoyl peroxide (NYPER BW available from NOF Corporation); while introducing nitrogen with gentle stirring and maintaining the liquid temperature inside the flask at around 63° C., polymerization reaction was carried out for tour hours to prepare an acrylic polymer solution (35 NV (non-volatiles)).

The acrylic polymer solution was diluted with toluene to 29% NV. To 100 parts (NV) of acrylic polymer in this solution, was added 3 parts of crosslinking agent (TETRAD C available from Mitsubishi Gas Chemical Company, Inc.). The resultant was allowed to stir and mix for about one minute while keeping the temperature near 25° C. Was further mixed 2.0 parts of Phosphate A (trade name Phosphanol RP-710 available from Toho Chemical Industry Co., Ltd.; polyoxyethylene phenyl ether phosphate) to prepare a solvent-based PSA composition according to this Example. Using the resulting PSA composition, but otherwise in the same manner as Preparation Example B1, was obtained a protective sheet B10.

Examples 1-10

As the protective sheets for test Low-E glass plate A2, using protective sheets B1 to B10, respectively, the Low-E glass plate discoloration test was conducted. The results are shown in Table 1. Table 1 also summarizes each Example.

Examples 11-20

As the protective sheets for test Low-E glass plate A1, using protective sheets B1 to B10, respectively, the Low-E glass plate discoloration test was conducted. The results are shown in Table 2. Table 2 also summarizes each Example.

TABLE 1 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Ex. 7 Ex. 8 Ex. 9 Ex. 10 Low-E glass plate A2 A2 A2 A2 A2 A2 A2 A2 A2 A2 Layer constitution SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ Ag Ag Ag Ag Ag Ag Ag Ag Ag Ag SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ Protective sheet B1 B2 B3 B4 B5 B6 B7 B8 B9 B10 Phosphate A (pt) 0.1 1 2 4 — — — — — 2.0 Phosphate B (pt) — — — — 2.0 — — — — — Phosphate C (pt) — — — — — 2.0 — — — — Phosphite (pt) — — — — — — 2.0 — — — Phosphorous compound (pt) — — — — — — — — 2.0 — Low-E glass plate discoloration test Good Good Good Good Good Good Good Fail Fail Good

TABLE 2 Ex. 11 Ex. 12 Ex. 13 Ex. 14 Ex. 15 Ex. 16 Ex. 17 Ex. 18 Ex. 19 Ex. 20 Low-E glass plate A1 A1 A1 A1 A1 A1 A1 A1 A1 A1 Layer constitution TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ Ag Ag Ag Ag Ag Ag Ag Ag Ag Ag SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ SnO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ TiO₂ Protective sheet B1 B2 B3 B4 B5 B6 B7 B8 B9 B10 Phosphate A (pt) 0.1 1.0 2.0 4.0 — — — — — 2.0 Phosphate B (pt) — — — — 2.0 — — — — — Phosphate C (pt) — — — — — 2.0 — — — — Phosphite (pt) — — — — — — 2.0 — — — Phosphorous compound (pt) — — — — — — — — 2.0 — Low-E glass plate discoloration test Good Good Good Good Good Good Good Fail Fail Good

As shown in Table 1, with the protective sheets according to Examples 1 to 7 and 10 each having PSA layers comprising P—OR-group-containing phosphorous compounds, discoloration was not observed in the Low-E glass plate discoloration test. On the other hand, in Example 8 fee of a phosphorous compound and Example 9 using a P—OR-group-free phosphorous compound, discoloration was observed in the Low-E glass plate discoloration test. As shown in Table 2, Examples 11 to 20 showed similar results.

<Verification Test> Preparation Example A3

Low-E layers were laminated in the following order starting from the glass plate side: SnO₂ layer, TiO₂ layer. Ag layer, TiO₂ layer and SnO₂ layer (outermost layer). Otherwise, basically in the same manner as Preparation Example A1, was prepared a test Low-E glass plate A3.

Experiment 1

Was obtained a protective sheet having a PSA layer comprising Phosphate A (trade name Phosphanol RP-710 available from Toho Chemical Industry Co., Ltd.; polyoxyethylene phenyl ether phosphate), applied to the test Low-E glass plate A3, and removed after a prescribed period Subsequently, the Low-E layer of the Low-E glass plate A3 was subjected to cross section adjustment by an FIB (focused ion beam) microsampling method; using a field emission transmission electron microscope (FE-TEM: model JEM-2800 available from JEOL Ltd), FE-TEM analysis was conducted on the specimens at an accelerating voltage of 200 kV further, using an energy dispersive X-ray spectroscopy (EDX) analyzer (product name NORAN System 7 available from Thermo Fisher Scientific Inc.), EDX elemental analysis was conducted. FIG. 3 shows a TEM image. The TEM image and TEM-EDX analysis data verified that an approximately 5 nm thick film was formed on the outermost SnO₂ layer of the Low-E layer in the Low-E glass plate A3 and the film comprised Sn, C and P. The Low-E layer of the Low-E glass plate A3 was etched by Ar-GCIB (Ar gas cluster ion beam) to remove deposits (organic substances from the PSA, etc.). Subsequently, analysis was conducted by TOF-SIMS (Time-of-Flight Secondary Ion Mass Spectrometry). As a result of the analysis, because P elements were detected even under conditions with no carbon detection, the film elements were verified to be inorganic, but not of the PSA residue. In addition, was obtained a protective sheet having a PSA layer free of a phosphorous compound, applied to the test Low-E glass plate A3, and removed after a prescribed period. As described above, the Low-E layer of the Low-E glass plate A3 was analyzed by TEM-EDX and TOF-SIMS after Ar-GCIB etching; however, formation of film was not observed on the Low-E layer surface.

Experiment 2

Was obtained a protective sheet having a PSA layer comprising Phosphate A (trade name Phosphanol RP-710 available from Toho Chemical Industry Co., Ltd.; polyoxyethylene phenyl ether phosphate) and applied to the test Low-E glass plate A3. Several of this were obtained and stored, respectively, at room temperature (23° C.), at a high temperature (40° C.) and at a high temperature/high humidity (40° C., 92% RH). Several samples for the respective storage conditions were collected at one hour, at one day and at two weeks after the start of storage; the protective sheets were removed; the Low-E layers of the Low-E glass plates A3 were etched by Ar-GCIB; and deposits (organic substances from the PSA, etc.) were removed. Subsequently, by FSCA (Electron Spectroscopy for Chemical Analysis), P elements were quantified. As shown in Table 3, the results verified that P-containing layers had been formed after one day from the start of storage.

TABLE 3 High temp. High T/High H** P (atom %) RT* (40° C.) (40° C., 92% RH) Storage time 1 hour 0 0 0 1 day 0.2 0.3 0.3 2 weeks 0.2 0.2 0.3 *room temperature **high temperature/high humidtity

The results of the experimental examples show that Low-E layer alteration is prevented by a PSA comprising a P—OR-group-containing phosphorous compound to protect a Low-E glass plate having a Low-E layer that comprises a tin component. The verification test results have revealed that the tin component of the Low-E layer reacts with the phosphorous compound in the SA layer to form a layer of the reaction product. These results support the thought that the passivation film formed of the reaction product of the tin component of the Low-E layer and the phosphorous compound in the PSA layer blocks the entry of a component potentially causing Low-E layer alteration.

Although specific embodiments of the present invention have been described in detail above, these are merely for illustrations and do not limit the scope of the claims. The art according to the claims includes various modifications and changes made to the specific embodiments illustrated above.

REFERENCE SIGNS LIST

-   1: substrate layer -   1A: first face -   1B: second face -   2: PSA layer -   2A: adhesive face -   10: protective sheet -   100: Low-E glass plate -   110: glass substrate -   120: Low-E layer -   200: protective sheet -   300: glass unit -   320: another glass unit -   340: spacer 

1. A method for protecting a Low-E glass plate, the method comprising a step of applying a protective sheet to a surface of a Low-E glass plate including a Low-E layer, wherein the Low-E layer comprises a tin component, and the pressure-sensitive adhesive layer comprises a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group.
 2. The method according to claim 1, wherein after the protective sheet is applied to the Low-E glass plate, a film is newly formed on/in the Low-E layer and the film comprises P and Sn as its constituent elements.
 3. The method according to claim 2, wherein the film exists on an outer surface of the Low-E layer.
 4. The method according to claim 2, wherein the film exists internal to the Low-E layer.
 5. The method according to claim 2, wherein the film is formed within 24 hours after the protective sheet is applied to the surface of the Low-E glass plate.
 6. The method according to claim 2, wherein the film has a thickness of 1 nm or greater and 20 nm or less.
 7. The method according to claim 1, wherein the phosphorous compound is selected between a phosphate and a phosphite.
 8. The method according to claim 1, wherein the Low-E layer comprises a tin-containing layer.
 9. The method according to claim 8, wherein the tin-containing layer is a tin oxide-containing layer.
 10. The method according to claim 1, the method further comprising a step of removing the protective sheet from the Low-E glass plate; and between the application and removal of the protective sheet to and from the Low-E glass plate, a step of subjecting the Low-E glass plate having the protective sheet applied thereon to at least one process selected from the group consisting of transportation, storage, processing, washing and handling.
 11. The method according to claim 1, wherein the Low-E glass plate has a width of 1 m or greater, the application of the protective sheet to the Low-E glass plate comprises a step of entirely covering one face of the Low-E glass plate with at least one said protective sheet.
 12. The method according to claim 1, wherein the protective sheet is adhered to the Low-E glass plate with a 180° peel strength of 5 N/20 mm or less.
 13. A method for preventing or inhibiting alteration to a Low-E glass plate that includes a Low-E layer, the method comprising a step of providing a phosphorous compound that has a P—OR group to the Low-E layer, wherein the Low-E layer comprises a tin component, and R in the P—OR group is a hydrogen atom or an organic group.
 14. The method according to claim 13, wherein after the phosphorous compound that has the P—OR group is provided to the Low-E layer, a film is newly formed on/in the Low-E layer and the film comprises P and Sn as its constituent elements.
 15. The method according to claim 13, wherein with a protective sheet that includes a pressure-sensitive adhesive layer comprising the phosphorous compound, the phosphorous compound is provided by applying a surface of the pressure-sensitive adhesive layer to the Low-E layer.
 16. A Low-E glass plate including a Low-E layer, wherein the Low-E layer comprises a film comprising P and Sn as its constituent elements.
 17. A method for producing a glass unit, the method comprising a step (A) of obtaining a Low-E glass plate including a Low-E layer; a step (B) of applying a protective sheet to a surface of the Low-E layer of the Low-E glass plate; an optional step (C) of subjecting the Low-E glass plate having the protective sheet applied thereon to at least one process selected from the group consisting of transportation, storage, processing, washing and handling; a step (D) of removing the protective sheet from the Low-E glass plate; and a step (E) of fabricating a glass unit using the Low-E glass plate; wherein the Low-E layer comprises a tin component, the protective sheet includes a pressure-sensitive adhesive layer, the pressure-sensitive adhesive layer comprises a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group.
 18. A laminate comprising: a Low-E glass plate; and a protective sheet protecting a surface of the Low-E glass plate, wherein the Low-E glass plate includes a Low-E layer comprising a tin component, the protective sheet includes a pressure-sensitive adhesive layer, and the pressure-sensitive adhesive layer comprises a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group.
 19. A protective sheet used on a Low-E glass plate, wherein the Low-E glass plate includes a Low-E layer comprising a tin component, the protective sheet includes a pressure-sensitive adhesive layer, and the pressure-sensitive adhesive layer comprises a phosphorous compound having a P—OR group, wherein R is a hydrogen atom or an organic group. 